Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.21 g/cm³ Show Material materials with Dichte of 1.21 g/cm³ | ASTM D 792 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 2.2 GPa Show Material materials with Biegemodul of 2.2 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Dehnung | 23.0 °C | 120 % Show Material materials with Dehnung of 120 % | ASTM D 638 | Type I, 50 mm/min |
Elastizitätsmodul | 23.0 °C | 2.41 GPa Show Material materials with Elastizitätsmodul of 2.41 GPa | ASTM D 638 | 50 mm/min |
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 86 MPa Show Material materials with Flexural yield strength of 86 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | 23.0 °C | 640 J/m Show Material materials with Impact strength, Izod notched, ASTM of 640 J/m | ASTM D 256 |
Streckgrenze | 23.0 °C | 58 MPa Show Material materials with Streckgrenze of 58 MPa | ASTM D 638 | Type I, 50 mm/min |
Zugfestigkeit | 23.0 °C | 44 MPa Show Material materials with Zugfestigkeit of 44 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 110 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 110 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 7.2E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 7.2E-5 1/K | ASTM E 831 | -40°C to 40°C |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7.2E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 7.2E-5 1/K | ASTM E 831 | -40°C to 40°C |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 35 g/10min Show Material materials with Schmelzmassenflussrate of 35 g/10min | ASTM D 1238 | 266°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.8 - 1 % Show Material materials with Schrumpfung of 0.8 - 1 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Heavy Vehicles,Recreational Vehicle | |
| Processing methods | Drying Temperature: 110°C, Drying Time: 4-6hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-280°C, Nozzle Temperature: 255-275°C, Front - Zone 3 Temperature: 260-280°C, Middle - Zone 2 Temperature: 255-275°C, Rear - Zone 1 Temperature: 250-270°C, Mold Temperature: 65-95°C, Back Pressure: 0.3-0.6MPa, Screw Speed: 50-80rpm, Shot to Cylinder Size: 50-80%, Vent Depth: 0.013-0.02mm | |