Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.34 g/cm³ Show Material materials with Dichte of 1.34 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.14 % Show Material materials with Wasserabsorption of 0.14 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 4 GPa Show Material materials with Biegemodul of 4 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 60 % Show Material materials with Dehnung of 60 % | ASTM D 638 | Type I, 5 mm/min | ||
Elastizitätsmodul | 23.0 °C | 4.6 GPa Show Material materials with Elastizitätsmodul of 4.6 GPa | ASTM D 638 | 5 mm/min | ||
Elongation at yield | 23.0 °C | 3.7 % Show Material materials with Elongation at yield of 3.7 % | ASTM D 638 | Type I, 5 mm/min | ||
Flexural yield strength | 23.0 °C | 98 MPa Show Material materials with Flexural yield strength of 98 MPa | ISO 178 | 2 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 105 MPa Show Material materials with Hardness, Ball Indentation of 105 MPa | ISO 2039-1 | ||
Impact strength, Izod notched, ASTM | -30.0 °C | 70 J/m Show Material materials with Impact strength, Izod notched, ASTM of 70 J/m | ASTM D 256 | ||
23.0 °C | 90 J/m Show Material materials with Impact strength, Izod notched, ASTM of 90 J/m | ASTM D 256 | |||
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 7 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 7 kJ/m² | ISO 179/1eA | ||
23.0 °C | 11 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 11 kJ/m² | ISO 179/1eA | |||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 6 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 6 kJ/m² | ISO 180/1A | ||
23.0 °C | 10 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 10 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 61 MPa Show Material materials with Streckgrenze of 61 MPa | ASTM D 638 | Type I, 5 mm/min | ||
Zugfestigkeit | 23.0 °C | 45 MPa Show Material materials with Zugfestigkeit of 45 MPa | ASTM D 638 | Type I, 5 mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | No break @ 23°C | ISO 179/2C | ||||
Schlagzähigkeit, Izod ungekerbt | No break @ 23°C | ISO 180/1U | ||||
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 131 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 131 °C | ISO 75/Bf | 0.45 MPa | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 4.3E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 4.3E-5 1/K | ASTM E 831 | -40°C to 40°C |
Vicat-Erweichungstemperatur | 137 °C Show Material materials with Vicat-Erweichungstemperatur of 137 °C | ASTM D 1525 | Rate B/50 | |
Wärmeleitfähigkeit | 23.0 °C | 0.2 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 0.2 W/(m·K) | ISO 8302 |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 6.4E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 6.4E-5 1/K | ASTM E 831 | -40°C to 40°C |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 8 g/10min Show Material materials with Schmelzmassenflussrate of 8 g/10min | ASTM D 1238 | 266°C/5.0 kg | |
Schmelzvolumenflussrate | 7 cm³/10min Show Material materials with Schmelzvolumenflussrate of 7 cm³/10min | ISO 1133 | 265°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.7 % Show Material materials with Schrumpfung of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Door Handle,Electronic Components,Enclosures,Food Processor,Wireless Communications | |
| Processing methods | Drying Temperature: 110-120°C, Drying Time: 4-6hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 265-275°C, Nozzle Temperature: 260-275°C, Front - Zone 3 Temperature: 260-280°C, Middle - Zone 2 Temperature: 250-275°C, Rear - Zone 1 Temperature: 240-270°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-100°C | |