Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.22 g/cm³ Show Material materials with Dichte of 1.22 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.15 % Show Material materials with Wasserabsorption of 0.15 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.05 GPa Show Material materials with Biegemodul of 2.05 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 50 % Show Material materials with Dehnung of 50 % | ISO 527 | 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.15 GPa Show Material materials with Elastizitätsmodul of 2.15 GPa | ISO 527 | 1 mm/min | ||
Elongation at yield | 23.0 °C | 4.5 % Show Material materials with Elongation at yield of 4.5 % | ISO 527 | 50 mm/min | ||
Flexural yield strength | 23.0 °C | 80 MPa Show Material materials with Flexural yield strength of 80 MPa | ISO 178 | 2 mm/min | ||
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 15 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 15 kJ/m² | ISO 179/1eA | ||
23.0 °C | 50 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 50 kJ/m² | ISO 179/1eA | |||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 18 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 18 kJ/m² | ISO 180/1A | ||
-20.0 °C | 20 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 20 kJ/m² | ISO 180/1A | |||
-10.0 °C | 35 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 35 kJ/m² | ISO 180/1A | |||
23.0 °C | 40 - 45 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 40 - 45 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 54 MPa Show Material materials with Streckgrenze of 54 MPa | ISO 527 | 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 40 MPa Show Material materials with Zugfestigkeit of 40 MPa | ISO 527 | 50 mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | No break @ -30°C | ISO 179/2C | ||||
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 84 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 84 °C | ISO 75/Ae | 1.8 MPa | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 8.5E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 8.5E-5 1/K | ISO 11359-2 | -23°C to 80°C |
Vicat-Erweichungstemperatur | 120 °C Show Material materials with Vicat-Erweichungstemperatur of 120 °C | ISO 306 | Rate B/120 | |
Wärmeleitfähigkeit | 23.0 °C | 0.2 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 0.2 W/(m·K) | ISO 8302 |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 8E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 8E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt viscosity | 260.0 °C | 215 Pa·s Show Material materials with Melt viscosity of 215 Pa·s | ISO 11443 | 1500 sec⁻¹ |
Schmelzvolumenflussrate | 13 cm³/10min Show Material materials with Schmelzvolumenflussrate of 13 cm³/10min | ISO 1133 | 250°C/2.16 kg | |
Schrumpfung | 23.0 °C | 0.7 - 1 % Show Material materials with Schrumpfung of 0.7 - 1 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Auto Aftermarket,Cluster,Enclosures,Exterior,Front Grille,Interior,Spoiler,Trim | |
| Processing methods | Drying Temperature: 90-100°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 255-270°C, Nozzle Temperature: 250-265°C, Front - Zone 3 Temperature: 250-270°C, Middle - Zone 2 Temperature: 240-265°C, Rear - Zone 1 Temperature: 230-250°C, Hopper Temperature: 40-60°C, Mold Temperature: 60-80°C | |