| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.2 g/cm³ Show Material materials with Dichte of 1.2 g/cm³ | ASTM D 792 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 71 MPa Show Material materials with Biegefestigkeit of 71 MPa | ISO 178 |
Biegemodul | 23.0 °C | 2 GPa Show Material materials with Biegemodul of 2 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 150 % Show Material materials with Dehnung of 150 % | ASTM D 638 | Type I, 50 mm/min |
Elastizitätsmodul | 23.0 °C | 1.84 GPa Show Material materials with Elastizitätsmodul of 1.84 GPa | ASTM D 638 | 50 mm/min |
Elongation at yield | 23.0 °C | 5 % Show Material materials with Elongation at yield of 5 % | ASTM D 638 | Type I, 50 mm/min |
Flexural yield strength | 23.0 °C | 83 MPa Show Material materials with Flexural yield strength of 83 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Impact strength, Izod notched, ASTM | 23.0 °C | 660 J/m Show Material materials with Impact strength, Izod notched, ASTM of 660 J/m | ASTM D 256 |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 9 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 9 kJ/m² | ISO 180/1A |
Streckgrenze | 23.0 °C | 49 MPa Show Material materials with Streckgrenze of 49 MPa | ASTM D 638 | Type I, 50 mm/min |
Zugfestigkeit | 23.0 °C | 52 MPa Show Material materials with Zugfestigkeit of 52 MPa | ASTM D 638 | Type I, 50 mm/min |
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 88 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 88 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.15E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.15E-4 1/K | ASTM E 831 | -40°C to 40°C |
Vicat-Erweichungstemperatur | 108 °C Show Material materials with Vicat-Erweichungstemperatur of 108 °C | ASTM D 1525 | Rate B/50 | |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.05E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.05E-4 1/K | ASTM E 831 | -40°C to 40°C |
Optisch
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 21 g/10min Show Material materials with Schmelzmassenflussrate of 21 g/10min | ASTM D 1238 | 265°C/2.16kgf | |
Schmelzvolumenflussrate | 21 cm³/10min Show Material materials with Schmelzvolumenflussrate of 21 cm³/10min | ISO 1133 | 265°C/2.16 kg | |
Schrumpfung | 23.0 °C | 0.4 - 0.8 % Show Material materials with Schrumpfung of 0.4 - 0.8 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.5 - 0.7 % Show Material materials with Schrumpfung, diagonal of 0.5 - 0.7 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Air Conditioning,Circuit Protection,Data Transfer,Enclosure/Housing/Cover,Enclosures,Forward Lighting,Head Protection,Non-LED Lighting,Personal Computing,Plumbing,Power Manangement,Pump,Renal and Blood Handling,Small Appliance,Vacuum Cleaner,Wireless Communications | |
| Processing methods | Drying Temperature: 80-95°C, Drying Time: 3-5hrs, Drying Time (Cumulative): 8hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 250-270°C, Nozzle Temperature: 250-270°C, Front - Zone 3 Temperature: 250-270°C, Middle - Zone 2 Temperature: 245-265°C, Rear - Zone 1 Temperature: 240-250°C, Mold Temperature: 45-60°C, Back Pressure: 0.2-0.5MPa, Screw Speed: 20-100rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.013-0.02mm | |