Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.27 g/cm³ Show Material materials with Dichte of 1.27 g/cm³ | ASTM D 792 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 4 GPa Show Material materials with Biegemodul of 4 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 50 % Show Material materials with Dehnung of 50 % | ISO 527 | 5 mm/min |
Elastizitätsmodul | 23.0 °C | 4.3 GPa Show Material materials with Elastizitätsmodul of 4.3 GPa | ASTM D 638 | 5 mm/min |
Elongation at yield | 23.0 °C | 4 % Show Material materials with Elongation at yield of 4 % | ASTM D 638 | Type I, 5 mm/min |
Flexural yield strength | 23.0 °C | 100 MPa Show Material materials with Flexural yield strength of 100 MPa | ISO 178 | 2 mm/min |
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA |
23.0 °C | 37 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 37 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 8 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 8 kJ/m² | ISO 180/1A |
23.0 °C | 15 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 15 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 56 MPa Show Material materials with Streckgrenze of 56 MPa | ASTM D 638 | Type I, 5 mm/min |
Zugfestigkeit | 23.0 °C | 47 MPa Show Material materials with Zugfestigkeit of 47 MPa | ASTM D 638 | Type I, 5 mm/min |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 120 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 120 °C | ASTM D 648 | 1.82 MPa, 3.2mm, unannealed | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 4.6E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 4.6E-5 1/K | ASTM E 831 | -40°C to 40°C |
Vicat-Erweichungstemperatur | 138 °C Show Material materials with Vicat-Erweichungstemperatur of 138 °C | ISO 306 | Rate B/50 | |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 6.1E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 6.1E-5 1/K | ASTM E 831 | -40°C to 40°C |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzvolumenflussrate | 12 cm³/10min Show Material materials with Schmelzvolumenflussrate of 12 cm³/10min | ISO 1133 | 265°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.7 % Show Material materials with Schrumpfung of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.5 - 0.7 % Show Material materials with Schrumpfung, diagonal of 0.5 - 0.7 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Applique,Console,Door Handle,Doors Hardware/Trim,Exterior Trim,Exterior,Overhead | |
Processing methods | Drying Temperature: 120-125°C, Drying Time: 4-6hrs, Maximum Moisture Content: 0.01%, Melt Temperature: 270-300°C, Nozzle Temperature: 260-290°C, Front - Zone 3 Temperature: 270-300°C, Middle - Zone 2 Temperature: 265-290°C, Rear - Zone 1 Temperature: 260-270°C, Mold Temperature: 60-100°C, Back Pressure: 0.3-0.7MPa, Screw Speed: 40-70rpm, Shot to Cylinder Size: 30-80%, Vent Depth: 0.038-0.076mm |