Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.14 g/cm³ Show Material materials with Dichte of 1.14 g/cm³ | ASTM D 792 |
Wasserabsorption | 23.0 °C | 0.15 % Show Material materials with Wasserabsorption of 0.15 % | ISO 62 | 23°C, 50% RH |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.2 GPa Show Material materials with Biegemodul of 2.2 GPa | ISO 178 | 2 mm/min | ||
Dehnung | 23.0 °C | 115 % Show Material materials with Dehnung of 115 % | ASTM D 638 | Type I, 50 mm/min | ||
Elastizitätsmodul | 23.0 °C | 2.3 GPa Show Material materials with Elastizitätsmodul of 2.3 GPa | ASTM D 638 | 5 mm/min | ||
Elongation at yield | 23.0 °C | 4.7 % Show Material materials with Elongation at yield of 4.7 % | ASTM D 638 | Type I, 50 mm/min | ||
Flexural yield strength | 23.0 °C | 83 MPa Show Material materials with Flexural yield strength of 83 MPa | ISO 178 | 2 mm/min | ||
Impact strength, Izod notched, ASTM | -30.0 °C | 480 J/m Show Material materials with Impact strength, Izod notched, ASTM of 480 J/m | ASTM D 256 | ||
23.0 °C | 640 J/m Show Material materials with Impact strength, Izod notched, ASTM of 640 J/m | ASTM D 256 | |||
Schlagfestigkeit, Charpy gekerbt | -30.0 °C | 45 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 45 kJ/m² | ISO 179/1eA | ||
23.0 °C | 60 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 60 kJ/m² | ISO 179/1eA | |||
Schlagzähigkeit, Izod gekerbt | -30.0 °C | 45 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 45 kJ/m² | ISO 180/1A | ||
23.0 °C | 55 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 55 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 55 MPa Show Material materials with Streckgrenze of 55 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Zugfestigkeit | 23.0 °C | 52 MPa Show Material materials with Zugfestigkeit of 52 MPa | ASTM D 638 | Type I, 50 mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | No break @ 23,-30°C | ISO 179/1eU | ||||
Schlagzähigkeit, Izod ungekerbt | No break @ 23,-30°C | ISO 180/1U | ||||
Thermisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 126 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 126 °C | ISO 75/Bf | 0.45 MPa | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 7E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 7E-5 1/K | ASTM E 831 | -40°C to 40°C |
Vicat-Erweichungstemperatur | 127 °C Show Material materials with Vicat-Erweichungstemperatur of 127 °C | ASTM D 1525 | Rate B/50 | |
Wärmeleitfähigkeit | 23.0 °C | 0.2 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 0.2 W/(m·K) | ISO 8302 |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 7E-5 1/K | ASTM E 831 | -40°C to 40°C |
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Durchschlagfestigkeit | 23.0 °C | 17 kV/mm Show Material materials with Durchschlagfestigkeit of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt viscosity | 260.0 °C | 195 Pa·s Show Material materials with Melt viscosity of 195 Pa·s | ISO 11443 | 1500 sec⁻¹ |
Schmelzmassenflussrate | 22 g/10min Show Material materials with Schmelzmassenflussrate of 22 g/10min | ASTM D 1238 | 260°C/5.0 kgf | |
Schmelzvolumenflussrate | 18 cm³/10min Show Material materials with Schmelzvolumenflussrate of 18 cm³/10min | ISO 1133 | 260°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.5 - 0.7 % Show Material materials with Schrumpfung of 0.5 - 0.7 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.5 - 0.7 % Show Material materials with Schrumpfung, diagonal of 0.5 - 0.7 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Applique,Audio,Auto Aftermarket,Cluster,Console,Data Transfer,Displays,Document Handling,Doors Hardware/Trim,Electronic Components,Enclosure/Housing/Cover,Enclosures,Energy Management,EV Infrastructure,Exterior Mirror,Exterior Rail Components,Exterior Trim,Forward Lighting,Front End,Front Grille,Glove Box,Headliner,Heavy Vehicles,Infotainment/Telematic,Interior,Meter Gas,Motorcycle,Non-LED Lighting,Overhead,Personal Computing,Personal Water Craft,Rail,Rear/Signal Lighting,Recreational Vehicle,Seat,Spoiler,Structure,Trim,Water Treatment/Filtration | |
| Processing methods | Drying Temperature: 95-105°C, Drying Time: 2-4hrs, Maximum Moisture Content: 0.02%, Melt Temperature: 260-290°C, Nozzle Temperature: 240-280°C, Front - Zone 3 Temperature: 250-290°C, Middle - Zone 2 Temperature: 250-290°C, Rear - Zone 1 Temperature: 230-260°C, Hopper Temperature: 60-80°C, Mold Temperature: 60-90°C | |