Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.19 g/cm³ Show Material materials with Dichte of 1.19 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 2.27 GPa Show Material materials with Biegemodul of 2.27 GPa | ISO 178 | 2 mm/min |
Dehnung | 23.0 °C | 46.7 % Show Material materials with Dehnung of 46.7 % | ISO 527 | 50 mm/min |
Elastizitätsmodul | 23.0 °C | 2.32 GPa Show Material materials with Elastizitätsmodul of 2.32 GPa | ISO 527 | 1 mm/min |
Elongation at yield | 23.0 °C | 5.2 % Show Material materials with Elongation at yield of 5.2 % | ISO 527 | 50 mm/min |
Flexural yield strength | 23.0 °C | 93 MPa Show Material materials with Flexural yield strength of 93 MPa | ISO 178 | 2 mm/min |
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 12 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 12 kJ/m² | ISO 179/1eA |
-30.0 °C | 14 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 14 kJ/m² | ISO 179/1eA | |
23.0 °C | 25 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 25 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Izod gekerbt | -40.0 °C | 8 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 8 kJ/m² | ISO 180/1A |
-30.0 °C | 8 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 8 kJ/m² | ISO 180/1A | |
23.0 °C | 14 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 14 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 60 MPa Show Material materials with Streckgrenze of 60 MPa | ISO 527 | 50 mm/min |
Zugfestigkeit | 23.0 °C | 45 MPa Show Material materials with Zugfestigkeit of 45 MPa | ISO 527 | 50 mm/min |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 125 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 125 °C | ISO 75/Bf | 0.45 MPa | |
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6.7E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 6.7E-5 1/K | ISO 11359-2 | -30°C to 80°C |
Vicat-Erweichungstemperatur | 126 °C Show Material materials with Vicat-Erweichungstemperatur of 126 °C | ISO 306 | Rate B/50 | |
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7.6E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 7.6E-5 1/K | ISO 11359-2 | -30°C to 80°C |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzvolumenflussrate | 28 cm³/10min Show Material materials with Schmelzvolumenflussrate of 28 cm³/10min | ISO 1133 | 260°C/5.0 kg | |
Schrumpfung | 23.0 °C | 0.6 - 0.9 % Show Material materials with Schrumpfung of 0.6 - 0.9 % | SABIC method | 3.2 mm |
Schrumpfung, diagonal | 23.0 °C | 0.6 - 0.9 % Show Material materials with Schrumpfung, diagonal of 0.6 - 0.9 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Exterior Mirror,Overhead | |
Processing methods | Drying Temperature: 95-105°C, Drying Time: 3-4hrs, Maximum Moisture Content: 0.04%, Melt Temperature: 265-285°C, Nozzle Temperature: 260-275°C, Front - Zone 3 Temperature: 240-270°C, Middle - Zone 2 Temperature: 250-275°C, Rear - Zone 1 Temperature: 260-280°C, Mold Temperature: 50-80°C, Back Pressure: 0.3-1MPa, Screw Speed: 30-80rpm, Shot to Cylinder Size: 40-80%, Vent Depth: 0.038-0.076mm |