Allgemein
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 195 MPa Show Material materials with Biegefestigkeit of 195 MPa | ISO 178 |
Dehnung | 23.0 °C | 3.3 % Show Material materials with Dehnung of 3.3 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 8.5 GPa Show Material materials with Elastizitätsmodul of 8.5 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.34 [-] Show Material materials with Poissonzahl of 0.34 [-] | |
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA |
23.0 °C | 13 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 13 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 70 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 70 kJ/m² | ISO 179/1eU |
Zugfestigkeit | 23.0 °C | 125 MPa Show Material materials with Zugfestigkeit of 125 MPa | ISO 527-1/-2 |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Glasübergangstemperatur | 65 °C Show Material materials with Glasübergangstemperatur of 65 °C | ISO 11357-1/-2 | 18°F/min | |
Heat deflection temperature, 0.45 MPa | 222 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 222 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 207 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 207 °C | ISO 75-1/-2 | |
Relative temperature index, mechanical strength | 192 °C Show Material materials with Relative temperature index, mechanical strength of 192 °C | IEC 60216-1 | 5000 hours | |
Schmelzpunkt | 225 °C Show Material materials with Schmelzpunkt of 225 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Oxygen index: 20 %, Glow Wire Flammability Index, 120mil: 750 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 31 mm/min |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.9 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 3.9 [-] | IEC 62631-2-1 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 4.1 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 4.1 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 5.7E-3 [-] Show Material materials with Dissipation factor, 100Hz of 5.7E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Durchschlagfestigkeit | 23.0 °C | 42 kV/mm Show Material materials with Durchschlagfestigkeit of 42 kV/mm | IEC 60243-1 |
Kriechstromfestigkeit | 23.0 °C | 0 V Show Material materials with Kriechstromfestigkeit of 0 V | UL 746A |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Material materials with Surface resistivity of 1.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt viscosity | 250.0 °C | 230 Pa·s Show Material materials with Melt viscosity of 230 Pa·s | ISO 11443 | @ 1000 sec-1, 250°C |
Schmelzvolumenflussrate | 8 cm³/10min Show Material materials with Schmelzvolumenflussrate of 8 cm³/10min | ISO 1133 | |
Schrumpfung | 23.0 °C | 0.3 % Show Material materials with Schrumpfung of 0.3 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.1 % Show Material materials with Schrumpfung, diagonal of 1.1 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Fillers | 30% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |