Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.31 g/cm³ Show Material materials with Dichte of 1.31 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dehnung | 23.0 °C | 13 % Show Material materials with Dehnung of 13 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 2.6 GPa Show Material materials with Elastizitätsmodul of 2.6 GPa | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 10 % Show Material materials with Elongation at yield of 10 % | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.38 [-] Show Material materials with Poissonzahl of 0.38 [-] | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 4 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 4 kJ/m² | ISO 179/1eA |
Streckgrenze | 23.0 °C | 60 MPa Show Material materials with Streckgrenze of 60 MPa | ISO 527-1/-2 |
Thermisch
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 50 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 50 °C | ISO 75-1/-2 | |
Schmelzpunkt | 224 °C Show Material materials with Schmelzpunkt of 224 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: 24 mm/min | ||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 50 g/10min Show Material materials with Schmelzmassenflussrate of 50 g/10min | ISO 1133 | 250°C/2.16kg | |
Schrumpfung | 23.0 °C | 1.7 % Show Material materials with Schrumpfung of 1.7 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.6 % Show Material materials with Schrumpfung, diagonal of 1.6 % | ISO 294-4, 2577 |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 240°C, Min. melt temperature: 235°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C | |