Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.3 g/cm³ Show Material materials with Dichte of 1.3 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 85 MPa Show Material materials with Biegefestigkeit of 85 MPa | ISO 178 |
Biegemodul | 23.0 °C | 2.4 GPa Show Material materials with Biegemodul of 2.4 GPa | ISO 178 |
Dehnung | 23.0 °C | 500 % Show Material materials with Dehnung of 500 % | min. | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 2.6 GPa Show Material materials with Elastizitätsmodul of 2.6 GPa | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 4 % Show Material materials with Elongation at yield of 4 % | ISO 527-1/-2 |
Hardness, Ball Indentation | 23.0 °C | 139 MPa Show Material materials with Hardness, Ball Indentation of 139 MPa | ISO 2039-1 |
Poissonzahl | 23.0 °C | 0.38 [-] Show Material materials with Poissonzahl of 0.38 [-] | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 5 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 4 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 4 kJ/m² | ISO 180/1A |
Streckgrenze | 23.0 °C | 57 MPa Show Material materials with Streckgrenze of 57 MPa | ISO 527-1/-2 |
Thermisch
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 180 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 180 °C | ISO 75-1/-2 | annealed | |
Heat deflection temperature, 1.80 MPa | 60 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 60 °C | ISO 75-1/-2 | annealed | |
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 240mil | |
Relative temperature index, mechanical impact | 115 °C Show Material materials with Relative temperature index, mechanical impact of 115 °C | UL 746B | 240mil | |
Relative temperature index, mechanical strength | 120 °C Show Material materials with Relative temperature index, mechanical strength of 120 °C | UL 746B | 240mil | |
Schmelzpunkt | 225 °C Show Material materials with Schmelzpunkt of 225 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 3 mm, UL recognition: yes -, Oxygen index: 21 %, Glow Wire Flammability Index, 120mil: 700 °C, FMVSS Class: SE - | ||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.3 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 3.3 [-] | IEC 62631-2-1 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 3.4 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 3.4 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 5E-4 [-] Show Material materials with Dissipation factor, 100Hz of 5E-4 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Durchschlagfestigkeit | 23.0 °C | 39 kV/mm Show Material materials with Durchschlagfestigkeit of 39 kV/mm | IEC 60243-1 |
Kriechstromfestigkeit | 23.0 °C | 375 V Show Material materials with Kriechstromfestigkeit of 375 V | IEC 60112 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Material materials with Surface resistivity of 1.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 11 g/10min Show Material materials with Schmelzmassenflussrate of 11 g/10min | ISO 1133 | 250°C/2.16kg | |
Schrumpfung | 23.0 °C | 1.9 % Show Material materials with Schrumpfung of 1.9 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.9 % Show Material materials with Schrumpfung, diagonal of 1.9 % | ISO 294-4, 2577 |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C | |