Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.31 g/cm³ Show Material materials with Dichte of 1.31 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 2.5 GPa Show Material materials with Biegemodul of 2.5 GPa | ISO 178 |
Elastizitätsmodul | 23.0 °C | 2.6 GPa Show Material materials with Elastizitätsmodul of 2.6 GPa | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 10 % Show Material materials with Elongation at yield of 10 % | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.38 [-] Show Material materials with Poissonzahl of 0.38 [-] | |
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 2.9 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 2.9 kJ/m² | ISO 179/1eA |
23.0 °C | 3.4 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 3.4 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 276 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 276 kJ/m² | ISO 179/1eU |
Schlagzähigkeit, Izod ungekerbt | -40.0 °C | 3.8 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 3.8 kJ/m² | ISO 180/1A |
23.0 °C | 4.2 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 4.2 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 57 MPa Show Material materials with Streckgrenze of 57 MPa | ISO 527-1/-2 |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 147 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 147 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 65 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 65 °C | ISO 75-1/-2 | annealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.9E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.9E-4 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Schmelzpunkt | 223 °C Show Material materials with Schmelzpunkt of 223 °C | ISO 11357-1/-3 | 18°F/min | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.8E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.8E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Entflammbarkeit | FMVSS Class: SE | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 34 g/10min Show Material materials with Schmelzmassenflussrate of 34 g/10min | ISO 1133 | 250°C/2.16kg | |
Schrumpfung | 23.0 °C | 2 % Show Material materials with Schrumpfung of 2 % | ISO 294-4 | Annealed |
Schrumpfung, diagonal | 23.0 °C | 2 % Show Material materials with Schrumpfung, diagonal of 2 % | ISO 294-4 | Annealed |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C | |