Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.67 g/cm³ Show Material materials with Dichte of 1.67 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 57 MPa Show Material materials with Biegefestigkeit of 57 MPa | ISO 178 |
Biegemodul | 23.0 °C | 8.3 GPa Show Material materials with Biegemodul of 8.3 GPa | ISO 178 |
Dehnung | 23.0 °C | 1 % Show Material materials with Dehnung of 1 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 7.1 GPa Show Material materials with Elastizitätsmodul of 7.1 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.35 [-] Show Material materials with Poissonzahl of 0.35 [-] | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 2.4 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 2.4 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 7.9 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 7.9 kJ/m² | ISO 179/1eU |
Zugfestigkeit | 23.0 °C | 39 MPa Show Material materials with Zugfestigkeit of 39 MPa | ISO 527-1/-2 |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 197 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 197 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 127 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 127 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.8E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.8E-5 1/K | ISO 11359-1/-2 | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 2.8E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 2.8E-5 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, Glow Wire Flammability Index, 30mil: 960 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 675 °C, Glow Wire Ignition Temperature, 60mil: 675 °C, Glow Wire Ignition Temperature, 120mil: 750 °C | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Volume resistivity | 23.0 °C | 1.00E+8 Ω·cm Show Material materials with Volume resistivity of 1.00E+8 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 40% Carbon Powder | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Max. regrind level: 15%, Melt Temperature Optimum: 275°C, Min. melt temperature: 260°C, Max. melt temperature: 290°C, Mold Temperature Optimum: 110°C, Min. mold temperature: 100°C, Max. mold temperature: 120°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C | |