Allgemein
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 180 MPa Show Material materials with Biegefestigkeit of 180 MPa | ISO 178 |
Dehnung | 23.0 °C | 3.2 % Show Material materials with Dehnung of 3.2 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 8.5 GPa Show Material materials with Elastizitätsmodul of 8.5 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.34 [-] Show Material materials with Poissonzahl of 0.34 [-] | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 12 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 12 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 70 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 70 kJ/m² | ISO 179/1eU |
Zugfestigkeit | 23.0 °C | 120 MPa Show Material materials with Zugfestigkeit of 120 MPa | ISO 527-1/-2 |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Glasübergangstemperatur | 65 °C Show Material materials with Glasübergangstemperatur of 65 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 1.80 MPa | 205 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 205 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 2.2E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.2E-5 1/K | ISO 11359-1/-2 | ||
Relative temperature index, mechanical strength | 192 °C Show Material materials with Relative temperature index, mechanical strength of 192 °C | IEC 60216-1 | 5000 hours | |||
Schmelzpunkt | 225 °C Show Material materials with Schmelzpunkt of 225 °C | ISO 11357-1/-3 | 18°F/min | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.9E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.9E-4 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Oxygen index: 20 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: 30 mm/min | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Durchschlagfestigkeit | 23.0 °C | 34 kV/mm Show Material materials with Durchschlagfestigkeit of 34 kV/mm | IEC 60243-1 |
Kriechstromfestigkeit | 23.0 °C | 1 V Show Material materials with Kriechstromfestigkeit of 1 V | UL 746A |
Surface resistivity | 23.0 °C | 1.00E+15 Ω/sq Show Material materials with Surface resistivity of 1.00E+15 Ω/sq | min. | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt viscosity | 250.0 °C | 230 Pa·s Show Material materials with Melt viscosity of 230 Pa·s | ISO 11443 | @ 1000 sec-1, 250°C |
Schmelzmassenflussrate | 13 g/10min Show Material materials with Schmelzmassenflussrate of 13 g/10min | ISO 1133 | 250°C/2.16kg | |
Schmelzvolumenflussrate | 8 cm³/10min Show Material materials with Schmelzvolumenflussrate of 8 cm³/10min | ISO 1133 | |
Schrumpfung | 23.0 °C | 0.3 % Show Material materials with Schrumpfung of 0.3 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.1 % Show Material materials with Schrumpfung, diagonal of 1.1 % | ISO 294-4, 2577 |
Technological properties
| Property | ||
|---|---|---|
| Fillers | 30% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C | |