Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.22 g/cm³ Show Material materials with Dichte of 1.22 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.31 % Show Material materials with Wasserabsorption of 0.31 % | Sim. to ISO 62 | 80mil |
Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Biegefestigkeit | 23.0 °C | 50 MPa Show Material materials with Biegefestigkeit of 50 MPa | ISO 178 | ||
Biegemodul | 23.0 °C | 1.55 GPa Show Material materials with Biegemodul of 1.55 GPa | ISO 178 | ||
Dehnung | 23.0 °C | 150 % Show Material materials with Dehnung of 150 % | ISO 527-1/-2 | 50mm/min | ||
Elastizitätsmodul | 23.0 °C | 1.7 GPa Show Material materials with Elastizitätsmodul of 1.7 GPa | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 7 % Show Material materials with Elongation at yield of 7 % | ISO 527-1/-2 | ||
Hardness, Rockwell R | 23.0 °C | 104 [-] Show Material materials with Hardness, Rockwell R of 104 [-] | ISO 2039-2 | ||
Poissonzahl | 23.0 °C | 0.42 [-] Show Material materials with Poissonzahl of 0.42 [-] | |||
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA | ||
-6.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA | |||
23.0 °C | 85 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 85 kJ/m² | ISO 179/1eA | |||
Schlagzähigkeit, Izod gekerbt | -40.0 °C | 270 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 270 kJ/m² | No Break @ 23,-30°C, ISO180/1A | ||
Schlagzähigkeit, Izod ungekerbt | -40.0 °C | 10 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 10 kJ/m² | ISO 180/1A | ||
-30.0 °C | 15 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 15 kJ/m² | ISO 180/1A | |||
23.0 °C | 60 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 60 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 38 MPa Show Material materials with Streckgrenze of 38 MPa | ISO 527-1/-2 | ||
Zugfestigkeit | 23.0 °C | 30 MPa Show Material materials with Zugfestigkeit of 30 MPa | ISO 527-1/-2 | 50mm/min | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-6°C, ISO 179/1eA |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 145 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 145 °C | ISO 75-1/-2 | annealed | |||
Heat deflection temperature, 1.80 MPa | 50 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 50 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 2.3E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2.3E-4 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Relative temperature index, electrical | 75 °C Show Material materials with Relative temperature index, electrical of 75 °C | UL 746B | 30mil | |||
Relative temperature index, mechanical impact | 75 °C Show Material materials with Relative temperature index, mechanical impact of 75 °C | UL 746B | 30mil | |||
Relative temperature index, mechanical strength | 75 °C Show Material materials with Relative temperature index, mechanical strength of 75 °C | UL 746B | 30mil | |||
Schmelzpunkt | 225 °C Show Material materials with Schmelzpunkt of 225 °C | ISO 11357-1/-3 | 18°F/min | |||
Spezifische Wärmekapazität | 23.0 °C | 2100 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 2100 J/(kg·K) | of melt | ||
Vicat-Erweichungstemperatur | 125 °C Show Material materials with Vicat-Erweichungstemperatur of 125 °C | ISO 306 | 90°F/h, 11 lbf | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.9E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.9E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Entflammbarkeit | Burning Behav. at thickness h: HB class, Thickness tested: 0.8 mm, UL recognition: yes -, Oxygen index: 19 %, Glow Wire Flammability Index, 80mil: 700 °C, Glow Wire Flammability Index, 120mil: 700 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 38 mm/min |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.4 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 3.4 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 100Hz of 0.02 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Durchschlagfestigkeit | 23.0 °C | 27 kV/mm Show Material materials with Durchschlagfestigkeit of 27 kV/mm | IEC 60243-1 |
Kriechstromfestigkeit | 23.0 °C | 600 V Show Material materials with Kriechstromfestigkeit of 600 V | IEC 60112 |
Surface resistivity | 23.0 °C | 1.00E+15 Ω/sq Show Material materials with Surface resistivity of 1.00E+15 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 5 g/10min Show Material materials with Schmelzmassenflussrate of 5 g/10min | ISO 1133 | 250°C/5kg | |
Schrumpfung | 23.0 °C | 2.5 % Show Material materials with Schrumpfung of 2.5 % | ISO 294-4 | Annealed |
Schrumpfung, diagonal | 23.0 °C | 1.9 % Show Material materials with Schrumpfung, diagonal of 1.9 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |