Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.42 g/cm³ Show Material materials with Dichte of 1.42 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 3 GPa Show Material materials with Biegemodul of 3 GPa | ISO 178 |
Dehnung | 23.0 °C | 40 % Show Material materials with Dehnung of 40 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 2.9 GPa Show Material materials with Elastizitätsmodul of 2.9 GPa | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 25 % Show Material materials with Elongation at yield of 25 % | ISO 527-1/-2 |
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 |
Härte, Rockwell M | 23.0 °C | 90 [-] Show Material materials with Härte, Rockwell M of 90 [-] | ISO 2039-2 |
Poissonzahl | 23.0 °C | 0.37 [-] Show Material materials with Poissonzahl of 0.37 [-] | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 11 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 11 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 365 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 365 kJ/m² | ISO 179/1eU |
Streckgrenze | 23.0 °C | 73 MPa Show Material materials with Streckgrenze of 73 MPa | ISO 527-1/-2 |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 161 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 161 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 94 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 94 °C | ISO 75-1/-2 | |
Schmelzpunkt | 178 °C Show Material materials with Schmelzpunkt of 178 °C | ISO 11357-1/-3 | 18°F/min | |
Vicat-Erweichungstemperatur | 175 °C Show Material materials with Vicat-Erweichungstemperatur of 175 °C | ISO 306 | 90°F, 2 lbf | |
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 3.96 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 3.96 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 2.7E-3 [-] Show Material materials with Dissipation factor, 100Hz of 2.7E-3 [-] | IEC 62631-2-1 |
Kriechstromfestigkeit | 23.0 °C | 600 V Show Material materials with Kriechstromfestigkeit of 600 V | IEC 60112 |
Surface resistivity | 23.0 °C | 2.00E+13 Ω/sq Show Material materials with Surface resistivity of 2.00E+13 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 2.4 g/10min Show Material materials with Schmelzmassenflussrate of 2.4 g/10min | ISO 1133 | 190°C/2.16kg | |
Schmelzvolumenflussrate | 2 cm³/10min Show Material materials with Schmelzvolumenflussrate of 2 cm³/10min | ISO 1133 | |
Schrumpfung | 23.0 °C | 2.1 % Show Material materials with Schrumpfung of 2.1 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.9 % Show Material materials with Schrumpfung, diagonal of 1.9 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 205°C, Min. melt temperature: 200°C, Max. melt temperature: 210°C, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 90-110MPa, Hold pressure time: 8s/mm |