Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.22 g/cm³ Show Material materials with Dichte of 1.22 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.5 % Show Material materials with Wasserabsorption of 0.5 % | Sim. to ISO 62 | Immersion 24h |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 0.29 GPa Show Material materials with Biegemodul of 0.29 GPa | ISO 178 |
Dehnung | 23.0 °C | 500 % Show Material materials with Dehnung of 500 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 0.28 GPa Show Material materials with Elastizitätsmodul of 0.28 GPa | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 31 % Show Material materials with Elongation at yield of 31 % | ISO 527-1/-2 |
Härte, Shore D | 23.0 °C | 63 [-] Show Material materials with Härte, Shore D of 63 [-] | max., ISO 7619-1 |
Poissonzahl | 23.0 °C | 0.48 [-] Show Material materials with Poissonzahl of 0.48 [-] | |
Reißfestigkeit | 23.0 °C | 158 kN/m Show Material materials with Reißfestigkeit of 158 kN/m | ISO 34-1 |
Reißfestigkeit, transversal | 23.0 °C | 145 kN/m Show Material materials with Reißfestigkeit, transversal of 145 kN/m | ISO 34-1 |
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 15 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 15 kJ/m² | ISO 179/1eA |
-6.0 °C | 25 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 25 kJ/m² | ISO 179/1eA | |
23.0 °C | 120 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 120 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Izod ungekerbt | -40.0 °C | 19 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 19 kJ/m² | ISO 180/1A |
23.0 °C | 81 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 81 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 20 MPa Show Material materials with Streckgrenze of 20 MPa | ISO 527-1/-2 |
Zugfestigkeit | 23.0 °C | 43 MPa Show Material materials with Zugfestigkeit of 43 MPa | ISO 527-1/-2 |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Brittleness temperature | -96 °C Show Material materials with Brittleness temperature of -96 °C | ISO 974 | |||
Glasübergangstemperatur | 0 °C Show Material materials with Glasübergangstemperatur of 0 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 80 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 80 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 45 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 45 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.9E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.9E-4 1/K | ASTM E 831 | 55 - 160°C | ||
Relative temperature index, electrical | 85 °C Show Material materials with Relative temperature index, electrical of 85 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 85 °C Show Material materials with Relative temperature index, mechanical impact of 85 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 80 °C Show Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | 120mil | |||
Schmelzpunkt | 210 °C Show Material materials with Schmelzpunkt of 210 °C | ISO 11357-1/-3 | 18°F/min | |||
Spezifische Wärmekapazität | 23.0 °C | 2150 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 2150 J/(kg·K) | of melt | ||
Temperaturleitfähigkeit | 23.0 °C | 0 mm²/s Show Material materials with Temperaturleitfähigkeit of 0 mm²/s | |||
Vicat-Erweichungstemperatur | 195 °C Show Material materials with Vicat-Erweichungstemperatur of 195 °C | ISO 306 | 90°F, 2 lbf | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.7E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.7E-4 1/K | ASTM E 831 | 23 - 55°C | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 3 mm, UL recognition: yes -, Oxygen index: 21 %, FMVSS Class: SE - |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 4.1 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 4.1 [-] | IEC 62631-2-1 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 4.6 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 4.6 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 100Hz of 0.01 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.04 [-] Show Material materials with Dissipation factor, 1MHz of 0.04 [-] | IEC 62631-2-1 |
Durchschlagfestigkeit | 23.0 °C | 20 kV/mm Show Material materials with Durchschlagfestigkeit of 20 kV/mm | IEC 60243-1 |
Surface resistivity | 23.0 °C | 1.00E+15 Ω/sq Show Material materials with Surface resistivity of 1.00E+15 Ω/sq | min. | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 8.00E+13 Ω·cm Show Material materials with Volume resistivity of 8.00E+13 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 9 g/10min Show Material materials with Schmelzmassenflussrate of 9 g/10min | ISO 1133 | 230°C/2.16kg | |
Schmelzvolumenflussrate | 8.5 cm³/10min Show Material materials with Schmelzvolumenflussrate of 8.5 cm³/10min | ISO 1133 | |
Schrumpfung | 23.0 °C | 1.5 % Show Material materials with Schrumpfung of 1.5 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.5 % Show Material materials with Schrumpfung, diagonal of 1.5 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 240°C, Min. melt temperature: 235°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 45°C, Max. mold temperature: 55°C, Hold pressure range: ≤70MPa |