Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.42 g/cm³ Show Material materials with Dichte of 1.42 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 2.9 GPa Show Material materials with Biegemodul of 2.9 GPa | ISO 178 |
Dehnung | 23.0 °C | 40 % Show Material materials with Dehnung of 40 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 3.1 GPa Show Material materials with Elastizitätsmodul of 3.1 GPa | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 22 % Show Material materials with Elongation at yield of 22 % | ISO 527-1/-2 |
Hardness, Rockwell R | 23.0 °C | 122 [-] Show Material materials with Hardness, Rockwell R of 122 [-] | ISO 2039-2 |
Härte, Rockwell M | 23.0 °C | 94 [-] Show Material materials with Härte, Rockwell M of 94 [-] | ISO 2039-2 |
Poissonzahl | 23.0 °C | 0.37 [-] Show Material materials with Poissonzahl of 0.37 [-] | |
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 9 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 9 kJ/m² | ISO 179/1eA |
23.0 °C | 10.5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10.5 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 10 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 10 kJ/m² | ISO 180/1A |
Streckgrenze | 23.0 °C | 73 MPa Show Material materials with Streckgrenze of 73 MPa | ISO 527-1/-2 |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 165 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 165 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 99 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 99 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.4E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.4E-4 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Relative temperature index, electrical | 50 °C Show Material materials with Relative temperature index, electrical of 50 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 50 °C Show Material materials with Relative temperature index, mechanical impact of 50 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 50 °C Show Material materials with Relative temperature index, mechanical strength of 50 °C | UL 746B | 120mil | |||
Schmelzpunkt | 178 °C Show Material materials with Schmelzpunkt of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.6E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.6E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dissipation factor, 1MHz | 23.0 °C | 6E-3 [-] Show Material materials with Dissipation factor, 1MHz of 6E-3 [-] | IEC 62631-2-1 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 2.3 g/10min Show Material materials with Schmelzmassenflussrate of 2.3 g/10min | ISO 1133 | 190°C/2.16kg | |
Schmelzvolumenflussrate | 1.9 cm³/10min Show Material materials with Schmelzvolumenflussrate of 1.9 cm³/10min | ISO 1133 | |
Schrumpfung | 23.0 °C | 1.8 % Show Material materials with Schrumpfung of 1.8 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 2 % Show Material materials with Schrumpfung, diagonal of 2 % | ISO 294-4, 2577 |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 215°C, Min. melt temperature: 210°C, Max. melt temperature: 220°C, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 90-110MPa, Hold pressure time: 7.5s/mm | |