Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.59 g/cm³ Show Material materials with Dichte of 1.59 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 142 MPa Show Material materials with Biegefestigkeit of 142 MPa | ISO 178 |
Dehnung | 23.0 °C | 4 % Show Material materials with Dehnung of 4 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 5.8 GPa Show Material materials with Elastizitätsmodul of 5.8 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.35 [-] Show Material materials with Poissonzahl of 0.35 [-] | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 9 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 9 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 55 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 55 kJ/m² | ISO 179/1eU |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 8 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 8 kJ/m² | ISO 180/1A |
Zugfestigkeit | 23.0 °C | 87 MPa Show Material materials with Zugfestigkeit of 87 MPa | ISO 527-1/-2 |
Thermisch
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 180 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 180 °C | ISO 75-1/-2 | |
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 240mil | |
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | 240mil | |
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | 240mil | |
Schmelzpunkt | 205 °C Show Material materials with Schmelzpunkt of 205 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 3 mm, UL recognition: yes -, Oxygen index: 31 %, Glow Wire Flammability Index, 120mil: 960 °C, FMVSS Class: DNI - | ||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 4.7 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 4.7 [-] | IEC 62631-2-1 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 5.2 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 5.2 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 100Hz of 0.02 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.03 [-] Show Material materials with Dissipation factor, 1MHz of 0.03 [-] | IEC 62631-2-1 |
Kriechstromfestigkeit | 23.0 °C | 225 V Show Material materials with Kriechstromfestigkeit of 225 V | IEC 60112 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Material materials with Surface resistivity of 1.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 20% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 80°C, Min. mold temperature: 30°C, Max. mold temperature: 130°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 150°C | |