Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.37 g/cm³ Show Material materials with Dichte of 1.37 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Biegemodul | 23.0 °C | 1.85 GPa Show Material materials with Biegemodul of 1.85 GPa | ISO 178 | ||
Dehnung | 23.0 °C | 500 % Show Material materials with Dehnung of 500 % | min. | ISO 527-1/-2 | ||
Elastizitätsmodul | 23.0 °C | 1.9 GPa Show Material materials with Elastizitätsmodul of 1.9 GPa | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 25 % Show Material materials with Elongation at yield of 25 % | ISO 527-1/-2 | ||
Hardness, Rockwell R | 23.0 °C | 113 [-] Show Material materials with Hardness, Rockwell R of 113 [-] | ISO 2039-2 | ||
Härte, Rockwell M | 23.0 °C | 64.6 [-] Show Material materials with Härte, Rockwell M of 64.6 [-] | ISO 2039-2 | ||
Poissonzahl | 23.0 °C | 0.41 [-] Show Material materials with Poissonzahl of 0.41 [-] | |||
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 14 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 14 kJ/m² | ISO 179/1eA | ||
23.0 °C | 25 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 25 kJ/m² | ISO 179/1eA | |||
Streckgrenze | 23.0 °C | 54 MPa Show Material materials with Streckgrenze of 54 MPa | ISO 527-1/-2 | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-6°C, ISO 179/1eA |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 126 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 126 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 71 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 71 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.2E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Schmelzpunkt | 178 °C Show Material materials with Schmelzpunkt of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
Vicat-Erweichungstemperatur | 173 °C Show Material materials with Vicat-Erweichungstemperatur of 173 °C | ISO 306 | 90°F, 2 lbf | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.2E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: 42 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 2.2 g/10min Show Material materials with Schmelzmassenflussrate of 2.2 g/10min | ISO 1133 | 190°C/2.16kg | |
Schmelzvolumenflussrate | 2 cm³/10min Show Material materials with Schmelzvolumenflussrate of 2 cm³/10min | ISO 1133 | |
Schrumpfung | 23.0 °C | 1.3 % Show Material materials with Schrumpfung of 1.3 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.5 % Show Material materials with Schrumpfung, diagonal of 1.5 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 4-8h, Processing Moisture Content: ≤0.05%, Melt Temperature Optimum: 205°C, Min. melt temperature: 200°C, Max. melt temperature: 210°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 50°C, Min. mold temperature: 40°C, Max. mold temperature: 60°C, Hold pressure range: 60-80MPa, Hold pressure time: 7.5s/mm |