Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.42 g/cm³ Show Material materials with Dichte of 1.42 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.9 % Show Material materials with Wasserabsorption of 0.9 % | Sim. to ISO 62 | 80mil |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 3 GPa Show Material materials with Biegemodul of 3 GPa | ISO 178 |
Dehnung | 23.0 °C | 40 % Show Material materials with Dehnung of 40 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 3.1 GPa Show Material materials with Elastizitätsmodul of 3.1 GPa | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 23 % Show Material materials with Elongation at yield of 23 % | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.37 [-] Show Material materials with Poissonzahl of 0.37 [-] | |
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA |
23.0 °C | 10.5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10.5 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -6.0 °C | 340 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 340 kJ/m² | No Break @ 23°C, ISO 179/1eU |
Schubmodule | 23.0 °C | 1.12 GPa Show Material materials with Schubmodule of 1.12 GPa | ISO 6721 |
Streckgrenze | 23.0 °C | 71 MPa Show Material materials with Streckgrenze of 71 MPa | ISO 527-1/-2 |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 165 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 165 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 100 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 100 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.1E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.1E-4 1/K | ISO 11359-1/-2 | ||
Schmelzpunkt | 178 °C Show Material materials with Schmelzpunkt of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.1E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.1E-4 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.5 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 3.5 [-] | IEC 62631-2-1 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 3.8 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 3.8 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 5.6E-3 [-] Show Material materials with Dissipation factor, 1MHz of 5.6E-3 [-] | IEC 62631-2-1 |
Kriechstromfestigkeit | 23.0 °C | 600 V Show Material materials with Kriechstromfestigkeit of 600 V | IEC 60112 |
Surface resistivity | 23.0 °C | 1.00E+15 Ω/sq Show Material materials with Surface resistivity of 1.00E+15 Ω/sq | min. | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 7 g/10min Show Material materials with Schmelzmassenflussrate of 7 g/10min | ISO 1133 | 190°C/2.16kg | |
Schmelzvolumenflussrate | 6 cm³/10min Show Material materials with Schmelzvolumenflussrate of 6 cm³/10min | ISO 1133 | |
Schrumpfung | 23.0 °C | 2.1 % Show Material materials with Schrumpfung of 2.1 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.8 % Show Material materials with Schrumpfung, diagonal of 1.8 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 215°C, Min. melt temperature: 210°C, Max. melt temperature: 220°C, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 80-100MPa, Hold pressure time: 8s/mm, Ejection temperature: 135°C |