Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.42 g/cm³ Show Material materials with Dichte of 1.42 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.27 % Show Material materials with Wasserabsorption of 0.27 % | Sim. to ISO 62 | Immersion 24h |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 93 MPa Show Material materials with Biegefestigkeit of 93 MPa | ISO 178 |
Biegemodul | 23.0 °C | 2.8 GPa Show Material materials with Biegemodul of 2.8 GPa | ISO 178 |
Dehnung | 23.0 °C | 45 % Show Material materials with Dehnung of 45 % | ISO 527-1/-2 |
Druckfestigkeit | 23.0 °C | 110 MPa Show Material materials with Druckfestigkeit of 110 MPa | ISO 604 |
Elastizitätsmodul | 23.0 °C | 2.9 GPa Show Material materials with Elastizitätsmodul of 2.9 GPa | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 26 % Show Material materials with Elongation at yield of 26 % | ISO 527-1/-2 |
Hardness, Ball Indentation | 23.0 °C | 173 MPa Show Material materials with Hardness, Ball Indentation of 173 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 121 [-] Show Material materials with Hardness, Rockwell R of 121 [-] | ISO 2039-2 |
Härte, Rockwell M | 23.0 °C | 90 [-] Show Material materials with Härte, Rockwell M of 90 [-] | ISO 2039-2 |
Poissonzahl | 23.0 °C | 0.37 [-] Show Material materials with Poissonzahl of 0.37 [-] | |
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 13 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 13 kJ/m² | ISO 179/1eA |
23.0 °C | 15 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 15 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -6.0 °C | 425 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 425 kJ/m² | No Break @ 23°C, ISO 179/1eU |
Schlagzähigkeit, Izod ungekerbt | -40.0 °C | 13 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 13 kJ/m² | ISO 180/1A |
23.0 °C | 14 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 14 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 71 MPa Show Material materials with Streckgrenze of 71 MPa | ISO 527-1/-2 |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 160 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 160 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 115 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 115 °C | ISO 75-1/-2 | annealed | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Relative temperature index, electrical | 105 °C Show Material materials with Relative temperature index, electrical of 105 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical impact | 85 °C Show Material materials with Relative temperature index, mechanical impact of 85 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical strength | 125 °C Show Material materials with Relative temperature index, mechanical strength of 125 °C | IEC 60216-1 | 5000 hours | |||
Schmelzpunkt | 178 °C Show Material materials with Schmelzpunkt of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
Spezifische Wärmekapazität | 23.0 °C | 3000 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 3000 J/(kg·K) | of melt | ||
Temperaturleitfähigkeit | 23.0 °C | 0 mm²/s Show Material materials with Temperaturleitfähigkeit of 0 mm²/s | |||
Vicat-Erweichungstemperatur | 175 °C Show Material materials with Vicat-Erweichungstemperatur of 175 °C | ISO 306 | 90°F, 2 lbf | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.8 mm, UL recognition: yes -, Glow Wire Flammability Index, 40mil: 550 °C, Glow Wire Flammability Index, 80mil: 550 °C, Glow Wire Flammability Index, 120mil: 550 °C, Glow Wire Ignition Temperature, 30mil: 550 °C, Glow Wire Ignition Temperature, 15mil: 550 °C, Glow Wire Ignition Temperature, 40mil: 550 °C, Glow Wire Ignition Temperature, 60mil: 550 °C, Glow Wire Ignition Temperature, 80mil: 550 °C, Glow Wire Ignition Temperature, 120mil: 550 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 40 mm/min |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.8 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 3.8 [-] | IEC 62631-2-1 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 3.9 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 3.9 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 1E-3 [-] Show Material materials with Dissipation factor, 100Hz of 1E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 5.5E-3 [-] Show Material materials with Dissipation factor, 1MHz of 5.5E-3 [-] | IEC 62631-2-1 |
Durchschlagfestigkeit | 23.0 °C | 41 kV/mm Show Material materials with Durchschlagfestigkeit of 41 kV/mm | IEC 60243-1 |
Kriechstromfestigkeit | 23.0 °C | 600 V Show Material materials with Kriechstromfestigkeit of 600 V | IEC 60112 |
Surface resistivity | 23.0 °C | 3.00E+13 Ω/sq Show Material materials with Surface resistivity of 3.00E+13 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 2.2 g/10min Show Material materials with Schmelzmassenflussrate of 2.2 g/10min | ISO 1133 | 190°C/2.16kg | |
Schmelzvolumenflussrate | 1.9 cm³/10min Show Material materials with Schmelzvolumenflussrate of 1.9 cm³/10min | ISO 1133 | |
Schrumpfung | 23.0 °C | 3 % Show Material materials with Schrumpfung of 3 % | ISO 294-4 | Annealed |
Schrumpfung, diagonal | 23.0 °C | 2.4 % Show Material materials with Schrumpfung, diagonal of 2.4 % | ISO 294-4 | Annealed |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 215°C, Min. melt temperature: 210°C, Max. melt temperature: 220°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 90-110MPa, Hold pressure time: 8s/mm |