Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.41 g/cm³ Show Material materials with Dichte of 1.41 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 1 % Show Material materials with Wasserabsorption of 1 % | Sim. to ISO 62 | 80mil |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 3.25 GPa Show Material materials with Biegemodul of 3.25 GPa | ISO 178 |
Dehnung | 23.0 °C | 22 % Show Material materials with Dehnung of 22 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 3.4 GPa Show Material materials with Elastizitätsmodul of 3.4 GPa | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 9 % Show Material materials with Elongation at yield of 9 % | ISO 527-1/-2 |
Hardness, Rockwell R | 23.0 °C | 119 [-] Show Material materials with Hardness, Rockwell R of 119 [-] | ISO 2039-2 |
Härte, Rockwell M | 23.0 °C | 93 [-] Show Material materials with Härte, Rockwell M of 93 [-] | ISO 2039-2 |
Poissonzahl | 23.0 °C | 0.37 [-] Show Material materials with Poissonzahl of 0.37 [-] | |
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 6.5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 6.5 kJ/m² | ISO 179/1eA |
23.0 °C | 7 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 7 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -6.0 °C | 210 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 210 kJ/m² | ISO 179/1eU |
23.0 °C | 190 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 190 kJ/m² | ISO 179/1eU | |
Streckgrenze | 23.0 °C | 71 MPa Show Material materials with Streckgrenze of 71 MPa | ISO 527-1/-2 |
Thermisch
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 0.45 MPa | 164 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 164 °C | ISO 75-1/-2 |
Heat deflection temperature, 1.80 MPa | 105 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 105 °C | ISO 75-1/-2 |
Schmelzpunkt | 178 °C Show Material materials with Schmelzpunkt of 178 °C | ISO 11357-1/-3 | 18°F/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 24 g/10min Show Material materials with Schmelzmassenflussrate of 24 g/10min | ISO 1133 | 190°C/2.16kg | |
Schmelzvolumenflussrate | 21 cm³/10min Show Material materials with Schmelzvolumenflussrate of 21 cm³/10min | ISO 1133 | |
Schrumpfung | 23.0 °C | 1.8 % Show Material materials with Schrumpfung of 1.8 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.7 % Show Material materials with Schrumpfung, diagonal of 1.7 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 215°C, Min. melt temperature: 210°C, Max. melt temperature: 220°C, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 80-100MPa, Hold pressure time: 7.5s/mm |