Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.54 g/cm³ Show Material materials with Dichte of 1.54 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.35 % Show Material materials with Wasserabsorption of 0.35 % | Sim. to ISO 62 | 80mil |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dehnung | 23.0 °C | 4.7 % Show Material materials with Dehnung of 4.7 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 3.9 GPa Show Material materials with Elastizitätsmodul of 3.9 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.36 [-] Show Material materials with Poissonzahl of 0.36 [-] | |
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 5 kJ/m² | ISO 179/1eA |
23.0 °C | 8.5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 8.5 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -6.0 °C | 40 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 40 kJ/m² | ISO 179/1eU |
23.0 °C | 46 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 46 kJ/m² | ISO 179/1eU | |
Zugfestigkeit | 23.0 °C | 70 MPa Show Material materials with Zugfestigkeit of 70 MPa | ISO 527-1/-2 |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 170 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 170 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 8.0 MPa | 66 °C Show Material materials with Heat deflection temperature, 8.0 MPa of 66 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 130 °C Show Material materials with Relative temperature index, electrical of 130 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical impact | 130 °C Show Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical strength | 130 °C Show Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | 240mil | |||
Schmelzpunkt | 205 °C Show Material materials with Schmelzpunkt of 205 °C | ISO 11357-1/-3 | 18°F/min | |||
Spezifische Wärmekapazität | 23.0 °C | 1970 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 1970 J/(kg·K) | of melt | ||
Vicat-Erweichungstemperatur | 180 °C Show Material materials with Vicat-Erweichungstemperatur of 180 °C | ISO 306 | 90°F/h, 11 lbf | |||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 0.75 mm, UL recognition: yes -, Oxygen index: 30 %, Glow Wire Flammability Index, 120mil: 960 °C, FMVSS Class: DNI - | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.8 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 3.8 [-] | IEC 62631-2-1 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 4 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 4 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 100Hz of 0.01 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Durchschlagfestigkeit | 23.0 °C | 16 kV/mm Show Material materials with Durchschlagfestigkeit of 16 kV/mm | IEC 60243-1 | Short Time, 2mm |
Kriechstromfestigkeit | 23.0 °C | 250 V Show Material materials with Kriechstromfestigkeit of 250 V | IEC 60112 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Material materials with Surface resistivity of 1.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Melt viscosity | 250.0 °C | 240 Pa·s Show Material materials with Melt viscosity of 240 Pa·s | ISO 11443 | @ 1000 sec-1, 250°C |
Schrumpfung | 23.0 °C | 0.7 % Show Material materials with Schrumpfung of 0.7 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.2 % Show Material materials with Schrumpfung, diagonal of 1.2 % | ISO 294-4, 2577 |
Technological properties
| Property | ||
|---|---|---|
| Fillers | 10% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.04%, Melt Temperature Optimum: 250°C, Min. melt temperature: 240°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 110°C, Min. mold temperature: 100°C, Max. mold temperature: 120°C, Hold pressure range: ≥60MPa, Hold pressure time: 3s/mm, Back pressure: As low as possible, Ejection temperature: 150°C | |