Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 1.04 GPa Show Material materials with Biegemodul of 1.04 GPa | ISO 178 |
Dehnung | 23.0 °C | 250 % Show Material materials with Dehnung of 250 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 1.05 GPa Show Material materials with Elastizitätsmodul of 1.05 GPa | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 19 % Show Material materials with Elongation at yield of 19 % | ISO 527-1/-2 |
Härte, Shore D | 23.0 °C | 71 [-] Show Material materials with Härte, Shore D of 71 [-] | max., ISO 7619-1 |
Poissonzahl | 23.0 °C | 0.45 [-] Show Material materials with Poissonzahl of 0.45 [-] | |
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 3.5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 3.5 kJ/m² | ISO 179/1eA |
23.0 °C | 5.5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 5.5 kJ/m² | ISO 179/1eA | |
Streckgrenze | 23.0 °C | 38 MPa Show Material materials with Streckgrenze of 38 MPa | ISO 527-1/-2 |
Zugfestigkeit | 23.0 °C | 49 MPa Show Material materials with Zugfestigkeit of 49 MPa | ISO 527-1/-2 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 110°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 250°C, Min. melt temperature: 245°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 45°C, Max. mold temperature: 55°C, Hold pressure range: ≥70MPa |