Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.59 g/cm³ Show Material materials with Dichte of 1.59 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 8.5 GPa Show Material materials with Biegemodul of 8.5 GPa | ISO 178 |
Elastizitätsmodul | 23.0 °C | 9.5 GPa Show Material materials with Elastizitätsmodul of 9.5 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.34 [-] Show Material materials with Poissonzahl of 0.34 [-] | |
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 7.5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 7.5 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 50 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 50 kJ/m² | ISO 179/1eU |
Thermisch
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 175 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 175 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 172 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 172 °C | ISO 75-1/-2 | |
Schmelzpunkt | 178 °C Show Material materials with Schmelzpunkt of 178 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: 44 mm/min | ||
Rheological Properties
| Property | Value | Comment |
|---|---|---|
Schmelzmassenflussrate | 7.5 g/10min Show Material materials with Schmelzmassenflussrate of 7.5 g/10min | ISO 1133 | 190°C/2.16kg |
Technological properties
| Property | ||
|---|---|---|
| Fillers | 25% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 215°C, Min. melt temperature: 210°C, Max. melt temperature: 220°C, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 80-100MPa, Hold pressure time: 8s/mm | |