Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.59 g/cm³ Show Material materials with Dichte of 1.59 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 1.26 % Show Material materials with Wasserabsorption of 1.26 % | Sim. to ISO 62 | 80mil |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 245 MPa Show Material materials with Biegefestigkeit of 245 MPa | ISO 178 |
Biegemodul | 23.0 °C | 9.15 GPa Show Material materials with Biegemodul of 9.15 GPa | ISO 178 |
Dehnung | 23.0 °C | 3 % Show Material materials with Dehnung of 3 % | ISO 527-1/-2 |
Druckfestigkeit | 23.0 °C | 210 MPa Show Material materials with Druckfestigkeit of 210 MPa | ISO 604 |
Elastizitätsmodul | 23.0 °C | 9.5 GPa Show Material materials with Elastizitätsmodul of 9.5 GPa | ISO 527-1/-2 |
Hardness, Rockwell R | 23.0 °C | 122 [-] Show Material materials with Hardness, Rockwell R of 122 [-] | ISO 2039-2 |
Härte, Rockwell M | 23.0 °C | 101 [-] Show Material materials with Härte, Rockwell M of 101 [-] | ISO 2039-2 |
Poissonzahl | 23.0 °C | 0.34 [-] Show Material materials with Poissonzahl of 0.34 [-] | |
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA |
23.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -6.0 °C | 50 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 50 kJ/m² | ISO 179/1eU |
23.0 °C | 60 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 60 kJ/m² | ISO 179/1eU | |
Zugfestigkeit | 23.0 °C | 160 MPa Show Material materials with Zugfestigkeit of 160 MPa | ISO 527-1/-2 |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 176 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 176 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 172 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 172 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 3.5E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 3.5E-5 1/K | ISO 11359-1/-2 | ||
Relative temperature index, electrical | 50 °C Show Material materials with Relative temperature index, electrical of 50 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 50 °C Show Material materials with Relative temperature index, mechanical impact of 50 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 50 °C Show Material materials with Relative temperature index, mechanical strength of 50 °C | UL 746B | 120mil | |||
Schmelzpunkt | 178 °C Show Material materials with Schmelzpunkt of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1E-4 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: 49 mm/min | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.8 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 3.8 [-] | IEC 62631-2-1 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 3.7 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 3.7 [-] | IEC 62631-2-1 |
Volume resistivity | 23.0 °C | 1.00E+14 Ω·cm Show Material materials with Volume resistivity of 1.00E+14 Ω·cm | IEC 62631-3-1 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 8 g/10min Show Material materials with Schmelzmassenflussrate of 8 g/10min | ISO 1133 | 190°C/2.16kg | |
Schrumpfung | 23.0 °C | 0.4 % Show Material materials with Schrumpfung of 0.4 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.2 % Show Material materials with Schrumpfung, diagonal of 1.2 % | ISO 294-4, 2577 |
Technological properties
| Property | ||
|---|---|---|
| Fillers | 25% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 215°C, Min. melt temperature: 210°C, Max. melt temperature: 220°C, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 80-100MPa, Hold pressure time: 8s/mm | |