Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of friction | 0.1 [-] Show Material materials with Coefficient of friction of 0.1 [-] | ASTM 1894 | 1h against itself | |
Dichte | 23.0 °C | 1.4 g/cm³ Show Material materials with Dichte of 1.4 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 1 % Show Material materials with Wasserabsorption of 1 % | Sim. to ISO 62 | 80mil |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 3 GPa Show Material materials with Biegemodul of 3 GPa | ISO 178 |
Dehnung | 23.0 °C | 30 % Show Material materials with Dehnung of 30 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 3.1 GPa Show Material materials with Elastizitätsmodul of 3.1 GPa | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 15 % Show Material materials with Elongation at yield of 15 % | ISO 527-1/-2 |
Hardness, Rockwell R | 23.0 °C | 119 [-] Show Material materials with Hardness, Rockwell R of 119 [-] | ISO 2039-2 |
Härte, Rockwell M | 23.0 °C | 91 [-] Show Material materials with Härte, Rockwell M of 91 [-] | ISO 2039-2 |
Poissonzahl | 23.0 °C | 0.37 [-] Show Material materials with Poissonzahl of 0.37 [-] | |
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 7.5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 7.5 kJ/m² | ISO 179/1eA |
23.0 °C | 6.5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 6.5 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -6.0 °C | 170 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 170 kJ/m² | ISO 179/1eU |
23.0 °C | 160 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 160 kJ/m² | ISO 179/1eU | |
Streckgrenze | 23.0 °C | 63 MPa Show Material materials with Streckgrenze of 63 MPa | ISO 527-1/-2 |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 160 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 160 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 100 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 100 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1E-4 1/K | ISO 11359-1/-2 | ||
Schmelzpunkt | 178 °C Show Material materials with Schmelzpunkt of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1E-4 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | Burning rate, Thickness 1 mm: 28 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 25 g/10min Show Material materials with Schmelzmassenflussrate of 25 g/10min | ISO 1133 | 190°C/2.16kg | |
Schmelzvolumenflussrate | 21 cm³/10min Show Material materials with Schmelzvolumenflussrate of 21 cm³/10min | ISO 1133 | |
Schrumpfung | 23.0 °C | 1.6 % Show Material materials with Schrumpfung of 1.6 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.8 % Show Material materials with Schrumpfung, diagonal of 1.8 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.05%, Melt Temperature Optimum: 215°C, Min. melt temperature: 210°C, Max. melt temperature: 220°C, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 80-100MPa, Hold pressure time: 8s/mm |