Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.56 g/cm³ Show Material materials with Dichte of 1.56 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 4.6 GPa Show Material materials with Biegemodul of 4.6 GPa | ISO 178 |
Dehnung | 23.0 °C | 10 % Show Material materials with Dehnung of 10 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 4.8 GPa Show Material materials with Elastizitätsmodul of 4.8 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.36 [-] Show Material materials with Poissonzahl of 0.36 [-] | |
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 3 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 3 kJ/m² | ISO 179/1eA |
23.0 °C | 3 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 3 kJ/m² | ISO 179/1eA | |
Zugfestigkeit | 23.0 °C | 52 MPa Show Material materials with Zugfestigkeit of 52 MPa | ISO 527-1/-2 |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 164 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 164 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 118 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 118 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 5.6E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 5.6E-5 1/K | ISO 11359-1/-2 | ||
Relative temperature index, electrical | 105 °C Show Material materials with Relative temperature index, electrical of 105 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical impact | 85 °C Show Material materials with Relative temperature index, mechanical impact of 85 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical strength | 90 °C Show Material materials with Relative temperature index, mechanical strength of 90 °C | UL 746B | 240mil | |||
Schmelzpunkt | 178 °C Show Material materials with Schmelzpunkt of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 9.2E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 9.2E-5 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 3 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 7 cm³/10min Show Material materials with Schmelzvolumenflussrate of 7 cm³/10min | ISO 1133 | |
Schrumpfung | 23.0 °C | 1.7 % Show Material materials with Schrumpfung of 1.7 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.1 % Show Material materials with Schrumpfung, diagonal of 1.1 % | ISO 294-4, 2577 |
Technological properties
| Property | ||
|---|---|---|
| Fillers | 20% Glass Fiber and Carbon Black | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 215°C, Min. melt temperature: 210°C, Max. melt temperature: 20°C, Mold Temperature Optimum: 90°C, Min. mold temperature: 80°C, Max. mold temperature: 100°C, Hold pressure range: 80-100MPa, Hold pressure time: 8s/mm | |