Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.25 g/cm³ Show Material materials with Dichte of 1.25 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 0.51 GPa Show Material materials with Biegemodul of 0.51 GPa | ISO 178 |
Dehnung | 23.0 °C | 590 % Show Material materials with Dehnung of 590 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 0.51 GPa Show Material materials with Elastizitätsmodul of 0.51 GPa | ISO 527-1/-2 |
Härte, Shore D | 23.0 °C | 71 [-] Show Material materials with Härte, Shore D of 71 [-] | max., ISO 7619-1 |
Poissonzahl | 23.0 °C | 0.47 [-] Show Material materials with Poissonzahl of 0.47 [-] | |
Reißfestigkeit | 23.0 °C | 180 kN/m Show Material materials with Reißfestigkeit of 180 kN/m | ISO 34-1 |
Reißfestigkeit, transversal | 23.0 °C | 165 kN/m Show Material materials with Reißfestigkeit, transversal of 165 kN/m | ISO 34-1 |
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 5 kJ/m² | ISO 179/1eA |
Zugfestigkeit | 23.0 °C | 50 MPa Show Material materials with Zugfestigkeit of 50 MPa | ISO 527-1/-2 |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Brittleness temperature | -68 °C Show Material materials with Brittleness temperature of -68 °C | ISO 974 | |
Schmelzpunkt | 216 °C Show Material materials with Schmelzpunkt of 216 °C | ISO 11357-1/-3 | 18°F/min | |
Vicat-Erweichungstemperatur | 204 °C Show Material materials with Vicat-Erweichungstemperatur of 204 °C | ISO 306 | 90°F, 2 lbf | |
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 110°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 245°C, Min. melt temperature: 235°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 45°C, Max. mold temperature: 55°C, Hold pressure range: ≤70MPa |