Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.37 g/cm³ Show Material materials with Dichte of 1.37 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.9 % Show Material materials with Wasserabsorption of 0.9 % | Sim. to ISO 62 | 80mil |
Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Biegemodul | 23.0 °C | 1.7 GPa Show Material materials with Biegemodul of 1.7 GPa | ISO 178 | ||
Dehnung | 23.0 °C | 500 % Show Material materials with Dehnung of 500 % | min. | ISO 527-1/-2 | ||
Elastizitätsmodul | 23.0 °C | 1.9 GPa Show Material materials with Elastizitätsmodul of 1.9 GPa | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 25 % Show Material materials with Elongation at yield of 25 % | ISO 527-1/-2 | ||
Hardness, Rockwell R | 23.0 °C | 113 [-] Show Material materials with Hardness, Rockwell R of 113 [-] | ISO 2039-2 | ||
Härte, Rockwell M | 23.0 °C | 59 [-] Show Material materials with Härte, Rockwell M of 59 [-] | ISO 2039-2 | ||
Poissonzahl | 23.0 °C | 0.41 [-] Show Material materials with Poissonzahl of 0.41 [-] | |||
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 14 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 14 kJ/m² | ISO 179/1eA | ||
23.0 °C | 26 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 26 kJ/m² | ISO 179/1eA | |||
Streckgrenze | 23.0 °C | 55 MPa Show Material materials with Streckgrenze of 55 MPa | ISO 527-1/-2 | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-6°C, ISO 179/1eA |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 130 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 130 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 72 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 72 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.2E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Relative temperature index, electrical | 100 °C Show Material materials with Relative temperature index, electrical of 100 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 85 °C Show Material materials with Relative temperature index, mechanical impact of 85 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 85 °C Show Material materials with Relative temperature index, mechanical strength of 85 °C | UL 746B | 120mil | |||
Schmelzpunkt | 178 °C Show Material materials with Schmelzpunkt of 178 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperaturleitfähigkeit | 23.0 °C | 0 mm²/s Show Material materials with Temperaturleitfähigkeit of 0 mm²/s | |||
Vicat-Erweichungstemperatur | 173 °C Show Material materials with Vicat-Erweichungstemperatur of 173 °C | ISO 306 | 90°F, 2 lbf | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.2E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.2E-4 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Glow Wire Flammability Index, 40mil: 550 °C, Glow Wire Flammability Index, 80mil: 550 °C, Glow Wire Flammability Index, 120mil: 550 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 42 mm/min |
Elektrisch
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 2.1 g/10min Show Material materials with Schmelzmassenflussrate of 2.1 g/10min | ISO 1133 | 190°C/2.16kg | |
Schmelzvolumenflussrate | 1.9 cm³/10min Show Material materials with Schmelzvolumenflussrate of 1.9 cm³/10min | ISO 1133 | |
Schrumpfung | 23.0 °C | 1.3 % Show Material materials with Schrumpfung of 1.3 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.5 % Show Material materials with Schrumpfung, diagonal of 1.5 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 4-8h, Processing Moisture Content: ≤0.05%, Melt Temperature Optimum: 205°C, Min. melt temperature: 200°C, Max. melt temperature: 210°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 50°C, Min. mold temperature: 40°C, Max. mold temperature: 60°C, Hold pressure range: 60-80MPa, Hold pressure time: 7.5s/mm |