Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.15 g/cm³ Show Material materials with Dichte of 1.15 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Biegemodul | 23.0 °C | 0.09 GPa Show Material materials with Biegemodul of 0.09 GPa | ISO 178 | ||
Dehnung | 23.0 °C | 300 % Show Material materials with Dehnung of 300 % | min. | ISO 527-1/-2 | ||
Elastizitätsmodul | 23.0 °C | 0.09 GPa Show Material materials with Elastizitätsmodul of 0.09 GPa | ISO 527-1/-2 | ||
Härte, Shore D | 23.0 °C | 45 [-] Show Material materials with Härte, Shore D of 45 [-] | max., ISO 7619-1 | ||
Reißfestigkeit | 23.0 °C | 117 kN/m Show Material materials with Reißfestigkeit of 117 kN/m | ISO 34-1 | ||
Reißfestigkeit, transversal | 23.0 °C | 119 kN/m Show Material materials with Reißfestigkeit, transversal of 119 kN/m | ISO 34-1 | ||
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 119 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 119 kJ/m² | No Break @ 23°C, ISO 179/1eU | ||
Zugfestigkeit | 23.0 °C | 30 MPa Show Material materials with Zugfestigkeit of 30 MPa | ISO 527-1/-2 | ||
Schlagzähigkeit, Izod ungekerbt | No Break @23,-40°C, ISO 180/1A |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Brittleness temperature | -100 °C Show Material materials with Brittleness temperature of -100 °C | ISO 974 | |
Glasübergangstemperatur | -45 °C Show Material materials with Glasübergangstemperatur of -45 °C | ISO 11357-1/-2 | 18°F/min | |
Heat deflection temperature, 0.45 MPa | 57 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 57 °C | ISO 75-1/-2 | |
Heat deflection temperature, 1.80 MPa | 41 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 41 °C | ISO 75-1/-2 | |
Schmelzpunkt | 204 °C Show Material materials with Schmelzpunkt of 204 °C | ISO 11357-1/-3 | 18°F/min | |
Vicat-Erweichungstemperatur | 164 °C Show Material materials with Vicat-Erweichungstemperatur of 164 °C | ISO 306 | 90°F, 2 lbf | |
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Property | Value | Comment |
---|---|---|
Schmelzmassenflussrate | 0.4 g/10min Show Material materials with Schmelzmassenflussrate of 0.4 g/10min | ISO 1133 | 220°C/10kg |
Schmelzvolumenflussrate | 4 cm³/10min Show Material materials with Schmelzvolumenflussrate of 4 cm³/10min | ISO 1133 |
Technological properties
Property | ||
---|---|---|
Fillers | Carbon Black | |
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 225°C, Min. melt temperature: 220°C, Max. melt temperature: 250°C |