Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.15 g/cm³ Show Material materials with Dichte of 1.15 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Biegemodul | 23.0 °C | 0.1 GPa Show Material materials with Biegemodul of 0.1 GPa | ISO 178 | ||
Dehnung | 23.0 °C | 202 % Show Material materials with Dehnung of 202 % | ISO 527-1/-2 | ||
Elastizitätsmodul | 23.0 °C | 0.1 GPa Show Material materials with Elastizitätsmodul of 0.1 GPa | ISO 527-1/-2 | ||
Härte, Shore D | 23.0 °C | 43 [-] Show Material materials with Härte, Shore D of 43 [-] | max., ISO 7619-1 | ||
Reißfestigkeit | 23.0 °C | 104 kN/m Show Material materials with Reißfestigkeit of 104 kN/m | ISO 34-1 | ||
Reißfestigkeit, transversal | 23.0 °C | 100 kN/m Show Material materials with Reißfestigkeit, transversal of 100 kN/m | ISO 34-1 | ||
Zugfestigkeit | 23.0 °C | 26 MPa Show Material materials with Zugfestigkeit of 26 MPa | ISO 527-1/-2 | ||
Schlagfestigkeit, Charpy gekerbt | No Break @ 23°C, ISO 179/1eU |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Glasübergangstemperatur | -25 °C Show Material materials with Glasübergangstemperatur of -25 °C | ISO 11357-1/-2 | 18°F/min | |
Heat deflection temperature, 0.45 MPa | 62 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 62 °C | ISO 75-1/-2 | |
Schmelzpunkt | 204 °C Show Material materials with Schmelzpunkt of 204 °C | ISO 11357-1/-3 | 18°F/min | |
Vicat-Erweichungstemperatur | 176 °C Show Material materials with Vicat-Erweichungstemperatur of 176 °C | ISO 306 | 90°F, 2 lbf | |
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 4.4 g/10min Show Material materials with Schmelzmassenflussrate of 4.4 g/10min | ISO 1133 | 230°C/10kg | |
Schrumpfung | 23.0 °C | 1.7 % Show Material materials with Schrumpfung of 1.7 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.6 % Show Material materials with Schrumpfung, diagonal of 1.6 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Fillers | Carbon Black | |
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 3-4h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 240°C, Min. melt temperature: 230°C, Max. melt temperature: 250°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 40°C, Max. mold temperature: 50°C |