Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.19 g/cm³ Show Material materials with Dichte of 1.19 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 35 % Show Material materials with Wasserabsorption of 35 % | Sim. to ISO 62 | Immersion 24h |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 0.08 GPa Show Material materials with Biegemodul of 0.08 GPa | ISO 178 | ||
Dehnung | 23.0 °C | 420 % Show Material materials with Dehnung of 420 % | ISO 527-1/-2 | ||
Elastizitätsmodul | 23.0 °C | 0.08 GPa Show Material materials with Elastizitätsmodul of 0.08 GPa | ISO 527-1/-2 | ||
Härte, Shore D | 23.0 °C | 40 [-] Show Material materials with Härte, Shore D of 40 [-] | max., ISO 7619-1 | ||
Poissonzahl | 23.0 °C | 0.49 [-] Show Material materials with Poissonzahl of 0.49 [-] | |||
Zugfestigkeit | 23.0 °C | 20 MPa Show Material materials with Zugfestigkeit of 20 MPa | ISO 527-1/-2 | ||
Schlagfestigkeit, Charpy gekerbt | No Break @ 23,-6°C, ISO 179/1eA | ||||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-6°C, ISO 179/1eA | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Schmelzpunkt | 200 °C Show Material materials with Schmelzpunkt of 200 °C | ISO 11357-1/-3 | 18°F/min | |||
Spezifische Wärmekapazität | 23.0 °C | 2100 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 2100 J/(kg·K) | of melt | ||
Temperaturleitfähigkeit | 23.0 °C | 0 mm²/s Show Material materials with Temperaturleitfähigkeit of 0 mm²/s | |||
Vicat-Erweichungstemperatur | 153 °C Show Material materials with Vicat-Erweichungstemperatur of 153 °C | ISO 306 | 90°F, 2 lbf | |||
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 14 cm³/10min Show Material materials with Schmelzvolumenflussrate of 14 cm³/10min | ISO 1133 | |
Schrumpfung | 23.0 °C | 1.4 % Show Material materials with Schrumpfung of 1.4 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.5 % Show Material materials with Schrumpfung, diagonal of 1.5 % | ISO 294-4, 2577 |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 230°C, Min. melt temperature: 220°C, Max. melt temperature: 240°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 40°C, Max. mold temperature: 50°C | |