Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.56 g/cm³ Show Material materials with Dichte of 1.56 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.05 % Show Material materials with Wasserabsorption of 0.05 % | Sim. to ISO 62 | Immersion 24h |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 210 MPa Show Material materials with Biegefestigkeit of 210 MPa | ISO 178 |
Biegemodul | 23.0 °C | 8.94 GPa Show Material materials with Biegemodul of 8.94 GPa | ISO 178 |
Dehnung | 23.0 °C | 2.1 % Show Material materials with Dehnung of 2.1 % | ISO 527-1/-2 |
Druckfestigkeit | 23.0 °C | 230 MPa Show Material materials with Druckfestigkeit of 230 MPa | ISO 604 |
Elastizitätsmodul | 23.0 °C | 10.2 GPa Show Material materials with Elastizitätsmodul of 10.2 GPa | ISO 527-1/-2 |
Hardness, Ball Indentation | 23.0 °C | 221 MPa Show Material materials with Hardness, Ball Indentation of 221 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 |
Poissonzahl | 23.0 °C | 0.34 [-] Show Material materials with Poissonzahl of 0.34 [-] | |
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 8 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 8 kJ/m² | ISO 179/1eA |
-6.0 °C | 8.5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 8.5 kJ/m² | ISO 179/1eA | |
23.0 °C | 9.5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 9.5 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -40.0 °C | 45 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 45 kJ/m² | ISO 179/1eU |
23.0 °C | 52 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 52 kJ/m² | ISO 179/1eU | |
Schlagzähigkeit, Izod gekerbt | -40.0 °C | 35 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 35 kJ/m² | ISO 180/1U |
23.0 °C | 45 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 45 kJ/m² | ISO 180/1U | |
Schlagzähigkeit, Izod ungekerbt | -40.0 °C | 8.5 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 8.5 kJ/m² | ISO 180/1A |
23.0 °C | 9.5 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 9.5 kJ/m² | ISO 180/1A | |
Zugfestigkeit | 23.0 °C | 150 MPa Show Material materials with Zugfestigkeit of 150 MPa | ISO 527-1/-2 |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 244 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 244 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 221 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 221 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical impact | 140 °C Show Material materials with Relative temperature index, mechanical impact of 140 °C | UL 746B | 240mil | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 240mil | |||
Schmelzpunkt | 250 °C Show Material materials with Schmelzpunkt of 250 °C | ISO 11357-1/-3 | 18°F/min | |||
Wärmeleitfähigkeit | 23.0 °C | 0.29 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 0.29 W/(m·K) | of solid | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.81 mm, UL recognition: yes -, Thickness tested: 0.75 mm, UL recognition: yes -, Glow Wire Flammability Index, 80mil: 800 °C, Glow Wire Flammability Index, 120mil: 900 °C, Glow Wire Ignition Temperature, 80mil: 825 °C, Glow Wire Ignition Temperature, 120mil: 825 °C, Glow Wire Temperature, No Flame, 40mil: 750 °C, Glow Wire Temperature, No Flame, 60mil: 750 °C, Glow Wire Temperature, No Flame, 80mil: 750 °C, Glow Wire Temperature, No Flame, 120mil: 825 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 38 mm/min | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 4.2 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 4.2 [-] | IEC 62631-2-1 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 4.5 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 4.5 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.03 [-] Show Material materials with Dissipation factor, 100Hz of 0.03 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Durchschlagfestigkeit | 23.0 °C | 22 kV/mm Show Material materials with Durchschlagfestigkeit of 22 kV/mm | IEC 60243-1 | Short Time, 23°C, 2mm |
Kriechstromfestigkeit | 23.0 °C | 250 V Show Material materials with Kriechstromfestigkeit of 250 V | IEC 60112 |
Surface resistivity | 23.0 °C | 1.00E+15 Ω/sq Show Material materials with Surface resistivity of 1.00E+15 Ω/sq | min. | IEC 62631-3-2 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 30% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 285°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 120°C, Min. mold temperature: 110°C, Max. mold temperature: 130°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C | |