Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.28 g/cm³ Show Material materials with Dichte of 1.28 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.3 % Show Material materials with Wasserabsorption of 0.3 % | Sim. to ISO 62 | Immersion 24h |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 1.2 GPa Show Material materials with Biegemodul of 1.2 GPa | ISO 178 |
Dehnung | 23.0 °C | 340 % Show Material materials with Dehnung of 340 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 1.2 GPa Show Material materials with Elastizitätsmodul of 1.2 GPa | ISO 527-1/-2 |
Elongation at yield | 23.0 °C | 19 % Show Material materials with Elongation at yield of 19 % | ISO 527-1/-2 |
Härte, Shore D | 23.0 °C | 76 [-] Show Material materials with Härte, Shore D of 76 [-] | max., ISO 7619-1 |
Poissonzahl | 23.0 °C | 0.44 [-] Show Material materials with Poissonzahl of 0.44 [-] | |
Reißfestigkeit | 23.0 °C | 228 kN/m Show Material materials with Reißfestigkeit of 228 kN/m | ISO 34-1 |
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 5 kJ/m² | ISO 179/1eA |
-6.0 °C | 5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 5 kJ/m² | ISO 179/1eA | |
23.0 °C | 15 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 15 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Izod ungekerbt | -40.0 °C | 5.5 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 5.5 kJ/m² | ISO 180/1A |
23.0 °C | 11 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 11 kJ/m² | ISO 180/1A | |
Streckgrenze | 23.0 °C | 36 MPa Show Material materials with Streckgrenze of 36 MPa | ISO 527-1/-2 |
Zugfestigkeit | 23.0 °C | 46 MPa Show Material materials with Zugfestigkeit of 46 MPa | ISO 527-1/-2 |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Brittleness temperature | -84 °C Show Material materials with Brittleness temperature of -84 °C | ISO 974 | |||
Glasübergangstemperatur | 50 °C Show Material materials with Glasübergangstemperatur of 50 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 0.45 MPa | 105 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 105 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.5E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.5E-4 1/K | ISO 11359-1/-2 | ||
Schmelzpunkt | 221 °C Show Material materials with Schmelzpunkt of 221 °C | ISO 11357-1/-3 | 18°F/min | |||
Vicat-Erweichungstemperatur | 213 °C Show Material materials with Vicat-Erweichungstemperatur of 213 °C | ISO 306 | 90°F, 2 lbf | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.5E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.5E-4 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 13 g/10min Show Material materials with Schmelzmassenflussrate of 13 g/10min | ISO 1133 | 240°C/2.16kg | |
Schmelzvolumenflussrate | 12 cm³/10min Show Material materials with Schmelzvolumenflussrate of 12 cm³/10min | ISO 1133 | |
Schrumpfung | 23.0 °C | 1.6 % Show Material materials with Schrumpfung of 1.6 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.6 % Show Material materials with Schrumpfung, diagonal of 1.6 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 110°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 250°C, Min. melt temperature: 245°C, Max. melt temperature: 260°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 45°C, Max. mold temperature: 55°C |