Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.13 g/cm³ Show Material materials with Dichte of 1.13 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 9.5 % Show Material materials with Wasserabsorption of 9.5 % | Sim. to ISO 62 | 80mil |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.3 GPa Show Material materials with Biegemodul of 2.3 GPa | ISO 178 | ||
Dehnung | 23.0 °C | 50 % Show Material materials with Dehnung of 50 % | ISO 527-1/-2 | 50mm/min | ||
Dehnung, transversal | 23.0 °C | 400 % Show Material materials with Dehnung, transversal of 400 % | ISO 527-3 | Film Properties | ||
Elastizitätsmodul | 23.0 °C | 2.9 GPa Show Material materials with Elastizitätsmodul of 2.9 GPa | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 4.5 % Show Material materials with Elongation at yield of 4.5 % | ISO 527-1/-2 | ||
Hardness, Ball Indentation | 23.0 °C | 170 MPa Show Material materials with Hardness, Ball Indentation of 170 MPa | ISO 2039-1 | ||
Hardness, Rockwell R | 23.0 °C | 119 [-] Show Material materials with Hardness, Rockwell R of 119 [-] | ISO 2039-2 | ||
Poissonzahl | 23.0 °C | 0.37 [-] Show Material materials with Poissonzahl of 0.37 [-] | |||
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 6 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 6 kJ/m² | ISO 179/1eA | ||
Schlagzähigkeit, Izod ungekerbt | -40.0 °C | 6 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 6 kJ/m² | ISO 180/1A | ||
23.0 °C | 6 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 6 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 80 MPa Show Material materials with Streckgrenze of 80 MPa | ISO 527-1/-2 | ||
Streckgrenze, transversal | 23.0 °C | 31 MPa Show Material materials with Streckgrenze, transversal of 31 MPa | ISO 527-3 | ||
Zugfestigkeit | 23.0 °C | 90 MPa Show Material materials with Zugfestigkeit of 90 MPa | ISO 527-3 | Film Properties | ||
Zugfestigkeit, transversal | 23.0 °C | 80 MPa Show Material materials with Zugfestigkeit, transversal of 80 MPa | ISO 527-3 | Film Properties | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-6,-40°C, ISO 179/1eA | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 160 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 160 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 55 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 55 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 7E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 7E-5 1/K | ISO 11359-1/-2 | ||
Schmelzpunkt | 221 °C Show Material materials with Schmelzpunkt of 221 °C | ISO 11357-1/-3 | 18°F/min | |||
Spezifische Wärmekapazität | 23.0 °C | 1680 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 1680 J/(kg·K) | of solid | ||
Wärmeleitfähigkeit | 23.0 °C | 0.24 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 0.24 W/(m·K) | of solid | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1E-4 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | Glow Wire Flammability Index, 40mil: 800 °C, Glow Wire Flammability Index, 120mil: 850 °C, Glow Wire Ignition Temperature, 30mil: 725 °C, Glow Wire Ignition Temperature, 15mil: 725 °C, Glow Wire Ignition Temperature, 40mil: 725 °C, Glow Wire Ignition Temperature, 60mil: 725 °C, Glow Wire Ignition Temperature, 80mil: 725 °C, Glow Wire Ignition Temperature, 120mil: 725 °C, Glow Wire Temperature, No Flame, 30mil: 700 °C, Glow Wire Temperature, No Flame, 40mil: 700 °C, Glow Wire Temperature, No Flame, 60mil: 700 °C, Glow Wire Temperature, No Flame, 80mil: 700 °C, Glow Wire Temperature, No Flame, 120mil: 700 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.5 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 3.5 [-] | IEC 62631-2-1 |
Kriechstromfestigkeit | 23.0 °C | 600 V Show Material materials with Kriechstromfestigkeit of 600 V | IEC 60112 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 270°C, Min. melt temperature: 260°C, Max. melt temperature: 280°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm | |