Allgemein
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 23.0 °C | 4 % Show Material materials with Dehnung of 4 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 6.6 GPa Show Material materials with Elastizitätsmodul of 6.6 GPa | ISO 527-1/-2 |
Hardness, Rockwell R | 23.0 °C | 121 [-] Show Material materials with Hardness, Rockwell R of 121 [-] | ISO 2039-2 |
Härte, Rockwell M | 23.0 °C | 95 [-] Show Material materials with Härte, Rockwell M of 95 [-] | ISO 2039-2 |
Poissonzahl | 23.0 °C | 0.35 [-] Show Material materials with Poissonzahl of 0.35 [-] | |
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 3 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 3 kJ/m² | ISO 179/1eA |
23.0 °C | 3.5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 3.5 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -6.0 °C | 25 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 25 kJ/m² | ISO 179/1eU |
23.0 °C | 35 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 35 kJ/m² | ISO 179/1eU | |
Zugfestigkeit | 23.0 °C | 85 MPa Show Material materials with Zugfestigkeit of 85 MPa | ISO 527-1/-2 |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 240 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 240 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 170 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 170 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6.5E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 6.5E-5 1/K | ISO 11359-1/-2 | ||
Relative temperature index, electrical | 120 °C Show Material materials with Relative temperature index, electrical of 120 °C | UL 746B | 60mil | |||
Relative temperature index, mechanical impact | 115 °C Show Material materials with Relative temperature index, mechanical impact of 115 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 115 °C Show Material materials with Relative temperature index, mechanical strength of 115 °C | UL 746B | 60mil | |||
Schmelzpunkt | 263 °C Show Material materials with Schmelzpunkt of 263 °C | ISO 11357-1/-3 | 18°F/min | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 9E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 9E-5 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.71 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.9 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 3.9 [-] | IEC 62631-2-1 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 4.5 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 4.5 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 100Hz of 0.01 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Durchschlagfestigkeit | 23.0 °C | 40 kV/mm Show Material materials with Durchschlagfestigkeit of 40 kV/mm | IEC 60243-1 |
Kriechstromfestigkeit | 23.0 °C | 575 V Show Material materials with Kriechstromfestigkeit of 575 V | IEC 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 40% Mineral Powder | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |