Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 0.89 g/cm³ Show Material materials with Dichte of 0.89 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 0.4 GPa Show Material materials with Biegemodul of 0.4 GPa | ISO 178 |
Dehnung | 23.0 °C | 130 % Show Material materials with Dehnung of 130 % | ISO 527-1/-2 |
Härte, Shore D | 23.0 °C | 40 [-] Show Material materials with Härte, Shore D of 40 [-] | ISO 7619-1 | 15 seconds |
Reißfestigkeit | 23.0 °C | 98 kN/m Show Material materials with Reißfestigkeit of 98 kN/m | ISO 34-1 |
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 72 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 72 kJ/m² | ISO 180/1A |
Zugfestigkeit | 23.0 °C | 16 MPa Show Material materials with Zugfestigkeit of 16 MPa | ISO 527-1/-2 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 6 cm³/10min Show Material materials with Schmelzvolumenflussrate of 6 cm³/10min | ISO 1133 | |
Schrumpfung | 23.0 °C | 1.1 % Show Material materials with Schrumpfung of 1.1 % | ISO 294-4, 2577 |
Technological properties
| Property | ||
|---|---|---|
| Color | Black | |
| Processing methods | Drying Recommended: no, Melt Temperature Optimum: 235°C, Mold Temperature Optimum: 30°C, Min. mold temperature: 20°C, Max. mold temperature: 40°C, Hold pressure range: as low as possible, Back pressure: 1MPa | |