Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.43 g/cm³ Show Material materials with Dichte of 1.43 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 1.9 % Show Material materials with Wasserabsorption of 1.9 % | Sim. to ISO 62 | Immersion 24h |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 0.15 GPa Show Material materials with Biegemodul of 0.15 GPa | ISO 178 |
Dehnung | 23.0 °C | 340 % Show Material materials with Dehnung of 340 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 0.14 GPa Show Material materials with Elastizitätsmodul of 0.14 GPa | ISO 527-1/-2 |
Härte, Shore D | 23.0 °C | 44 [-] Show Material materials with Härte, Shore D of 44 [-] | max., ISO 7619-1 |
Reißfestigkeit | 23.0 °C | 70 kN/m Show Material materials with Reißfestigkeit of 70 kN/m | ISO 34-1 |
Reißfestigkeit, transversal | 23.0 °C | 70 kN/m Show Material materials with Reißfestigkeit, transversal of 70 kN/m | ISO 34-1 |
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 5 kJ/m² | ISO 179/1eA |
-6.0 °C | 7 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 7 kJ/m² | ISO 179/1eA | |
23.0 °C | 40 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 40 kJ/m² | ISO 179/1eA | |
Zugfestigkeit | 23.0 °C | 13 MPa Show Material materials with Zugfestigkeit of 13 MPa | ISO 527-1/-2 |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Brittleness temperature | -48 °C Show Material materials with Brittleness temperature of -48 °C | ISO 974 | |||
Heat deflection temperature, 0.45 MPa | 46 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 46 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 41 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 41 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.5E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.5E-4 1/K | ISO 11359-1/-2 | ||
Relative temperature index, electrical | 50 °C Show Material materials with Relative temperature index, electrical of 50 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 50 °C Show Material materials with Relative temperature index, mechanical impact of 50 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 50 °C Show Material materials with Relative temperature index, mechanical strength of 50 °C | UL 746B | 120mil | |||
Schmelzpunkt | 170 °C Show Material materials with Schmelzpunkt of 170 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperaturleitfähigkeit | 23.0 °C | 0 mm²/s Show Material materials with Temperaturleitfähigkeit of 0 mm²/s | |||
Vicat-Erweichungstemperatur | 107 °C Show Material materials with Vicat-Erweichungstemperatur of 107 °C | ISO 306 | 90°F, 2 lbf | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.7E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.7E-4 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: V-0 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-0 class, Thickness tested: 3 mm, UL recognition: yes -, Oxygen index: 26 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Elektrisch
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 4 g/10min Show Material materials with Schmelzmassenflussrate of 4 g/10min | ISO 1133 | 190°C/2.16kg | |
Schmelzvolumenflussrate | 3.6 cm³/10min Show Material materials with Schmelzvolumenflussrate of 3.6 cm³/10min | ISO 1133 | |
Schrumpfung | 23.0 °C | 1.1 % Show Material materials with Schrumpfung of 1.1 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.1 % Show Material materials with Schrumpfung, diagonal of 1.1 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 200°C, Min. melt temperature: 190°C, Max. melt temperature: 210°C, Mold Temperature Optimum: 40°C, Min. mold temperature: 30°C, Max. mold temperature: 40°C |