Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.06 g/cm³ Show Material materials with Dichte of 1.06 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 3 % Show Material materials with Wasserabsorption of 3 % | Sim. to ISO 62 | 80mil |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.1 GPa Show Material materials with Biegemodul of 2.1 GPa | ISO 178 | ||
Dehnung | 23.0 °C | 30 % Show Material materials with Dehnung of 30 % | ISO 527-1/-2 | ||
Elastizitätsmodul | 23.0 °C | 2.4 GPa Show Material materials with Elastizitätsmodul of 2.4 GPa | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 4.4 % Show Material materials with Elongation at yield of 4.4 % | ISO 527-1/-2 | ||
Hardness, Ball Indentation | 23.0 °C | 170 MPa Show Material materials with Hardness, Ball Indentation of 170 MPa | ISO 2039-1 | ||
Poissonzahl | 23.0 °C | 0.38 [-] Show Material materials with Poissonzahl of 0.38 [-] | |||
Scherfestigkeit | 23.0 °C | 60 MPa Show Material materials with Scherfestigkeit of 60 MPa | ASTM D 732 | ||
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 5 kJ/m² | ISO 179/1eA | ||
23.0 °C | 4 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 4 kJ/m² | ISO 179/1eA | |||
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 5 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 5 kJ/m² | ISO 180/1A | ||
23.0 °C | 4 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 4 kJ/m² | ISO 180/1A | |||
Streckgrenze | 23.0 °C | 62 MPa Show Material materials with Streckgrenze of 62 MPa | ISO 527-1/-2 | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-6°C, ISO 179/1eA | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 135 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 135 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 62 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 62 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.7E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.7E-4 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Relative temperature index, electrical | 105 °C Show Material materials with Relative temperature index, electrical of 105 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 65 °C Show Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | 120mil | |||
Schmelzpunkt | 218 °C Show Material materials with Schmelzpunkt of 218 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperaturleitfähigkeit | 23.0 °C | 0 mm²/s Show Material materials with Temperaturleitfähigkeit of 0 mm²/s | |||
Vicat-Erweichungstemperatur | 180 °C Show Material materials with Vicat-Erweichungstemperatur of 180 °C | ISO 306 | 90°F/h, 11 lbf | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.8E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.8E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.86 mm, UL recognition: yes -, Oxygen index: 27 %, Glow Wire Flammability Index, 30mil: 825 °C, Glow Wire Flammability Index, 60mil: 775 °C, Glow Wire Flammability Index, 120mil: 925 °C, Glow Wire Ignition Temperature, 30mil: 700 °C, Glow Wire Ignition Temperature, 60mil: 700 °C, Glow Wire Ignition Temperature, 120mil: 700 °C, Glow Wire Temperature, No Flame, 40mil: 700 °C, Glow Wire Temperature, No Flame, 120mil: 750 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.2 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 3.2 [-] | IEC 62631-2-1 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 3.6 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 3.6 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 100Hz of 0.01 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Durchschlagfestigkeit | 23.0 °C | 22.6 kV/mm Show Material materials with Durchschlagfestigkeit of 22.6 kV/mm | IEC 60243-1 | Short Time, 2mm |
Kriechstromfestigkeit | 23.0 °C | 600 V Show Material materials with Kriechstromfestigkeit of 600 V | IEC 60112 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.15%, Melt Temperature Optimum: 250°C, Min. melt temperature: 230°C, Max. melt temperature: 290°C, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C | |