Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.67 g/cm³ Show Material materials with Dichte of 1.67 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dehnung | 23.0 °C | 2 % Show Material materials with Dehnung of 2 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 11 GPa Show Material materials with Elastizitätsmodul of 11 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.34 [-] Show Material materials with Poissonzahl of 0.34 [-] | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 9 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 9 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 40 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 40 kJ/m² | ISO 179/1eU |
Zugfestigkeit | 23.0 °C | 150 MPa Show Material materials with Zugfestigkeit of 150 MPa | ISO 527-1/-2 |
Thermisch
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 230 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 230 °C | ISO 75-1/-2 | |
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 240mil | |
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 120mil | |
Schmelzpunkt | 250 °C Show Material materials with Schmelzpunkt of 250 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | Burning Behav. at thickness h: V-2 class, Thickness tested: 0.8 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Kriechstromfestigkeit | 23.0 °C | 200 V Show Material materials with Kriechstromfestigkeit of 200 V | IEC 60112 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt viscosity | 280.0 °C | 210 Pa·s Show Material materials with Melt viscosity of 210 Pa·s | ISO 11443 | @ 1000 sec-1, 280°C |
Schrumpfung | 23.0 °C | 0.3 % Show Material materials with Schrumpfung of 0.3 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 0.9 % Show Material materials with Schrumpfung, diagonal of 0.9 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Fillers | 25% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 280°C, Min. melt temperature: 270°C, Max. melt temperature: 290°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 140°C, Min. mold temperature: 120°C, Max. mold temperature: 140°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |