Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.39 g/cm³ Show Material materials with Dichte of 1.39 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 2.5 % Show Material materials with Wasserabsorption of 2.5 % | Sim. to ISO 62 | 80mil |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 3.55 GPa Show Material materials with Biegemodul of 3.55 GPa | ISO 178 |
Dehnung | 23.0 °C | 5 % Show Material materials with Dehnung of 5 % | ISO 527-1/-2 |
Druckfestigkeit | 23.0 °C | 90 MPa Show Material materials with Druckfestigkeit of 90 MPa | ISO 604 |
Elastizitätsmodul | 23.0 °C | 4.7 GPa Show Material materials with Elastizitätsmodul of 4.7 GPa | ISO 527-1/-2 |
Hardness, Rockwell R | 23.0 °C | 111 [-] Show Material materials with Hardness, Rockwell R of 111 [-] | ISO 2039-2 |
Härte, Rockwell M | 23.0 °C | 58 [-] Show Material materials with Härte, Rockwell M of 58 [-] | ISO 2039-2 |
Poissonzahl | 23.0 °C | 0.36 [-] Show Material materials with Poissonzahl of 0.36 [-] | |
Scherfestigkeit | 23.0 °C | 40 MPa Show Material materials with Scherfestigkeit of 40 MPa | ASTM D 732 |
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 8 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 8 kJ/m² | ISO 179/1eA |
23.0 °C | 11 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 11 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -6.0 °C | 25 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 25 kJ/m² | ISO 179/1eU |
23.0 °C | 55 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 55 kJ/m² | ISO 179/1eU | |
Schlagzähigkeit, Izod ungekerbt | -30.0 °C | 7.7 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 7.7 kJ/m² | ISO 180/1A |
23.0 °C | 13 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 13 kJ/m² | ISO 180/1A | |
Zugfestigkeit | 23.0 °C | 79 MPa Show Material materials with Zugfestigkeit of 79 MPa | ISO 527-1/-2 |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 235 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 235 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 207 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 207 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.1E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.1E-4 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 120 °C Show Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 120mil | |||
Schmelzpunkt | 250 °C Show Material materials with Schmelzpunkt of 250 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperaturleitfähigkeit | 23.0 °C | 0 mm²/s Show Material materials with Temperaturleitfähigkeit of 0 mm²/s | |||
Vicat-Erweichungstemperatur | 205 °C Show Material materials with Vicat-Erweichungstemperatur of 205 °C | ISO 306 | 90°F/h, 11 lbf | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 3.2E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 3.2E-5 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Oxygen index: 19 %, Glow Wire Flammability Index, 30mil: 700 °C, Glow Wire Flammability Index, 40mil: 700 °C, Glow Wire Flammability Index, 60mil: 700 °C, Glow Wire Flammability Index, 80mil: 725 °C, Glow Wire Flammability Index, 120mil: 775 °C, Glow Wire Ignition Temperature, 30mil: 675 °C, Glow Wire Ignition Temperature, 40mil: 675 °C, Glow Wire Ignition Temperature, 60mil: 675 °C, Glow Wire Ignition Temperature, 80mil: 700 °C, Glow Wire Ignition Temperature, 120mil: 725 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: 33 mm/min |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.9 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 3.9 [-] | IEC 62631-2-1 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 4.5 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 4.5 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.07 [-] Show Material materials with Dissipation factor, 100Hz of 0.07 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Durchschlagfestigkeit | 23.0 °C | 38 kV/mm Show Material materials with Durchschlagfestigkeit of 38 kV/mm | IEC 60243-1 |
Kriechstromfestigkeit | 23.0 °C | 2 V Show Material materials with Kriechstromfestigkeit of 2 V | UL 746A |
Surface resistivity | 23.0 °C | 1.00E+13 Ω/sq Show Material materials with Surface resistivity of 1.00E+13 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+13 Ω·cm Show Material materials with Volume resistivity of 1.00E+13 Ω·cm | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 15% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 285°C, Min. melt temperature: 270°C, Max. melt temperature: 290°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 95°C, Min. mold temperature: 75°C, Max. mold temperature: 95°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C |