Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Biegemodul | 23.0 °C | 2.8 GPa Show Material materials with Biegemodul of 2.8 GPa | ISO 178 | ||
Dehnung | 23.0 °C | 18 % Show Material materials with Dehnung of 18 % | ISO 527-1/-2 | ||
Elastizitätsmodul | 23.0 °C | 3.1 GPa Show Material materials with Elastizitätsmodul of 3.1 GPa | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 4.5 % Show Material materials with Elongation at yield of 4.5 % | ISO 527-1/-2 | ||
Poissonzahl | 23.0 °C | 0.37 [-] Show Material materials with Poissonzahl of 0.37 [-] | |||
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 5 kJ/m² | ISO 179/1eA | ||
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 300 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 300 kJ/m² | ISO 180/1U | ||
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 5.5 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 5.5 kJ/m² | ISO 180/1A | ||
Streckgrenze | 23.0 °C | 85 MPa Show Material materials with Streckgrenze of 85 MPa | ISO 527-1/-2 | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23°C, ISO 179/1eU |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 200 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 200 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 70 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 70 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.2E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.2E-4 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 110 °C Show Material materials with Relative temperature index, mechanical impact of 110 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 125 °C Show Material materials with Relative temperature index, mechanical strength of 125 °C | UL 746B | 120mil | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1.8E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1.8E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: V-2 class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: V-2 class, Thickness tested: 0.71 mm, UL recognition: yes -, Glow Wire Flammability Index, 30mil: 850 °C, Glow Wire Flammability Index, 60mil: 960 °C, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 30mil: 725 °C, Glow Wire Ignition Temperature, 60mil: 725 °C, Glow Wire Ignition Temperature, 120mil: 725 °C, FMVSS Class: DNI - |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 290°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.4m/s, Mold Temperature Optimum: 70°C, Min. mold temperature: 50°C, Max. mold temperature: 90°C, Hold pressure range: 50-100MPa, Hold pressure time: 4s/mm, Ejection temperature: 190°C |