Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.37 g/cm³ Show Material materials with Dichte of 1.37 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegefestigkeit | 23.0 °C | 280 MPa Show Material materials with Biegefestigkeit of 280 MPa | ISO 178 |
Biegemodul | 23.0 °C | 9 GPa Show Material materials with Biegemodul of 9 GPa | ISO 178 |
Dehnung | 23.0 °C | 3 % Show Material materials with Dehnung of 3 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 10 GPa Show Material materials with Elastizitätsmodul of 10 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.34 [-] Show Material materials with Poissonzahl of 0.34 [-] | |
Schlagfestigkeit, Charpy gekerbt | -6.0 °C | 8 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 8 kJ/m² | ISO 179/1eA |
23.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 65 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 65 kJ/m² | ISO 179/1eU |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 10 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 10 kJ/m² | ISO 180/1A |
Zugfestigkeit | 23.0 °C | 190 MPa Show Material materials with Zugfestigkeit of 190 MPa | ISO 527-1/-2 |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Glasübergangstemperatur | 75 °C Show Material materials with Glasübergangstemperatur of 75 °C | ISO 11357-1/-2 | 18°F/min | |||
Heat deflection temperature, 1.80 MPa | 253 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 253 °C | ISO 75-1/-2 | |||
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 125 °C Show Material materials with Relative temperature index, mechanical impact of 125 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 120mil | |||
Schmelzpunkt | 262 °C Show Material materials with Schmelzpunkt of 262 °C | ISO 11357-1/-3 | 18°F/min | |||
Spezifische Wärmekapazität | 23.0 °C | 2220 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 2220 J/(kg·K) | of melt | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Oxygen index: 24 %, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min, Hot Wire Ignition, 30mil: 7 s, Hot Wire Ignition, 60mil: 7 s, Hot Wire Ignition, 120mil: 60 s |
Elektrisch
Property | Temperature | Value | Comment |
---|---|---|---|
Kriechstromfestigkeit | 23.0 °C | 400 V Show Material materials with Kriechstromfestigkeit of 400 V | IEC 60112 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 30% Glass Fiber | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm |