Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.24 g/cm³ Show Material materials with Dichte of 1.24 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 0.7 % Show Material materials with Wasserabsorption of 0.7 % | Sim. to ISO 62 | 80mil |
Mechanisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Biegemodul | 23.0 °C | 0.36 GPa Show Material materials with Biegemodul of 0.36 GPa | ISO 178 | ||
Dehnung | 23.0 °C | 490 % Show Material materials with Dehnung of 490 % | ISO 527-1/-2 | ||
Elastizitätsmodul | 23.0 °C | 0.36 GPa Show Material materials with Elastizitätsmodul of 0.36 GPa | ISO 527-1/-2 | ||
Elongation at yield | 23.0 °C | 29 % Show Material materials with Elongation at yield of 29 % | ISO 527-1/-2 | ||
Härte, Shore D | 23.0 °C | 63 [-] Show Material materials with Härte, Shore D of 63 [-] | max., ISO 7619-1 | ||
Poissonzahl | 23.0 °C | 0.48 [-] Show Material materials with Poissonzahl of 0.48 [-] | |||
Reißfestigkeit | 23.0 °C | 210 kN/m Show Material materials with Reißfestigkeit of 210 kN/m | ISO 34-1 | ||
Reißfestigkeit, transversal | 23.0 °C | 200 kN/m Show Material materials with Reißfestigkeit, transversal of 200 kN/m | ISO 34-1 | ||
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 10 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | No Break @ 23°C, ISO 179/1eU | ||
-6.0 °C | 14 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 14 kJ/m² | No Break @ 23°C, ISO 179/1eU | |||
Schlagzähigkeit, Izod ungekerbt | -40.0 °C | 9 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 9 kJ/m² | ISO 180/1A | ||
Streckgrenze | 23.0 °C | 22 MPa Show Material materials with Streckgrenze of 22 MPa | ISO 527-1/-2 | ||
Zugfestigkeit | 23.0 °C | 45 MPa Show Material materials with Zugfestigkeit of 45 MPa | ISO 527-1/-2 | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23,-6°C, ISO 179/1eA | ||||
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 85 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 85 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 2E-4 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2E-4 1/K | ISO 11359-1/-2 | ||
Schmelzpunkt | 211 °C Show Material materials with Schmelzpunkt of 211 °C | ISO 11357-1/-3 | 18°F/min | |||
Spezifische Wärmekapazität | 23.0 °C | 2070 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 2070 J/(kg·K) | of melt | ||
Temperaturleitfähigkeit | 23.0 °C | 0 mm²/s Show Material materials with Temperaturleitfähigkeit of 0 mm²/s | |||
Vicat-Erweichungstemperatur | 198 °C Show Material materials with Vicat-Erweichungstemperatur of 198 °C | ISO 306 | 90°F, 2 lbf | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 2E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 2E-4 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dissipation factor, 100Hz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 100Hz of 0.01 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 62631-2-1 |
Durchschlagfestigkeit | 23.0 °C | 18 kV/mm Show Material materials with Durchschlagfestigkeit of 18 kV/mm | IEC 60243-1 |
Kriechstromfestigkeit | 23.0 °C | 600 V Show Material materials with Kriechstromfestigkeit of 600 V | IEC 60112 |
Surface resistivity | 23.0 °C | 2.00E+14 Ω/sq Show Material materials with Surface resistivity of 2.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 7.00E+12 Ω·cm Show Material materials with Volume resistivity of 7.00E+12 Ω·cm | IEC 62631-3-1 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzvolumenflussrate | 5 cm³/10min Show Material materials with Schmelzvolumenflussrate of 5 cm³/10min | ISO 1133 | |
Schrumpfung | 23.0 °C | 1.7 % Show Material materials with Schrumpfung of 1.7 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 1.6 % Show Material materials with Schrumpfung, diagonal of 1.6 % | ISO 294-4, 2577 |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 110°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 240°C, Min. melt temperature: 230°C, Max. melt temperature: 250°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 40°C, Max. mold temperature: 50°C | |