Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.19 g/cm³ Show Material materials with Dichte of 1.19 g/cm³ | ISO 1183 |
Mechanisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Biegemodul | 23.0 °C | 0.19 GPa Show Material materials with Biegemodul of 0.19 GPa | ISO 178 | ||
Dehnung | 23.0 °C | 450 % Show Material materials with Dehnung of 450 % | ISO 527-1/-2 | ||
Elastizitätsmodul | 23.0 °C | 0.19 GPa Show Material materials with Elastizitätsmodul of 0.19 GPa | ISO 527-1/-2 | ||
Härte, Shore D | 23.0 °C | 56 [-] Show Material materials with Härte, Shore D of 56 [-] | max., ISO 7619-1 | ||
Poissonzahl | 23.0 °C | 0.48 [-] Show Material materials with Poissonzahl of 0.48 [-] | |||
Reißfestigkeit | 23.0 °C | 150 kN/m Show Material materials with Reißfestigkeit of 150 kN/m | ISO 34-1 | ||
Reißfestigkeit, transversal | 23.0 °C | 135 kN/m Show Material materials with Reißfestigkeit, transversal of 135 kN/m | ISO 34-1 | ||
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 19 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 19 kJ/m² | No Break @ 23°C, ISO 179/1eU | ||
-6.0 °C | 39 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 39 kJ/m² | No Break @ 23°C, ISO 179/1eU | |||
Schlagzähigkeit, Izod ungekerbt | -40.0 °C | 20 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 20 kJ/m² | ISO 180/1A | ||
Zugfestigkeit | 23.0 °C | 38 MPa Show Material materials with Zugfestigkeit of 38 MPa | ISO 527-1/-2 | ||
Schlagzähigkeit, Charpy ungekerbt | No Break @ 23°C, ISO 179/1eU |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Brittleness temperature | -54 °C Show Material materials with Brittleness temperature of -54 °C | ISO 974 | |||
Glasübergangstemperatur | -40 °C Show Material materials with Glasübergangstemperatur of -40 °C | ISO 11357-1/-2 | 18°F/min | |||
Schmelzpunkt | 214 °C Show Material materials with Schmelzpunkt of 214 °C | ISO 11357-1/-3 | 18°F/min | |||
Spezifische Wärmekapazität | 23.0 °C | 2150 J/(kg·K) Show Material materials with Spezifische Wärmekapazität of 2150 J/(kg·K) | of melt | ||
Vicat-Erweichungstemperatur | 182 °C Show Material materials with Vicat-Erweichungstemperatur of 182 °C | ISO 306 | 90°F, 2 lbf | |||
Entflammbarkeit | FMVSS Class: B -, Burning rate, Thickness 1 mm: 42 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Schmelzmassenflussrate | 9 g/10min Show Material materials with Schmelzmassenflussrate of 9 g/10min | ISO 1133 | 240°C/10kg | |
Schmelzvolumenflussrate | 9 cm³/10min Show Material materials with Schmelzvolumenflussrate of 9 cm³/10min | ISO 1133 | |
Schrumpfung | 23.0 °C | 2.2 % Show Material materials with Schrumpfung of 2.2 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 2.1 % Show Material materials with Schrumpfung, diagonal of 2.1 % | ISO 294-4, 2577 |
Technological properties
Property | ||
---|---|---|
Processing methods | Drying Recommended: yes, Drying Temperature: 100°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 245°C, Min. melt temperature: 240°C, Max. melt temperature: 255°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 40°C, Max. mold temperature: 55°C |