Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.39 g/cm³ Show Material materials with Dichte of 1.39 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegemodul | 23.0 °C | 4 GPa Show Material materials with Biegemodul of 4 GPa | ISO 178 |
Dehnung | 23.0 °C | 5 % Show Material materials with Dehnung of 5 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 4.5 GPa Show Material materials with Elastizitätsmodul of 4.5 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.36 [-] Show Material materials with Poissonzahl of 0.36 [-] | |
Schlagfestigkeit, Charpy gekerbt | 23.0 °C | 11 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 11 kJ/m² | ISO 179/1eA |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 55 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 55 kJ/m² | ISO 179/1eU |
Schlagzähigkeit, Izod ungekerbt | 23.0 °C | 11 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 11 kJ/m² | ISO 180/1A |
Zugfestigkeit | 23.0 °C | 80 MPa Show Material materials with Zugfestigkeit of 80 MPa | ISO 527-1/-2 |
Thermisch
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 190 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 190 °C | ISO 75-1/-2 | |
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 120mil | |
Relative temperature index, mechanical impact | 120 °C Show Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | 120mil | |
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 120mil | |
Schmelzpunkt | 250 °C Show Material materials with Schmelzpunkt of 250 °C | ISO 11357-1/-3 | 18°F/min | |
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.75 mm, UL recognition: yes -, Glow Wire Flammability Index, 30mil: 675 °C, Glow Wire Flammability Index, 40mil: 675 °C, Glow Wire Flammability Index, 60mil: 675 °C, Glow Wire Flammability Index, 80mil: 675 °C, Glow Wire Flammability Index, 120mil: 700 °C, Glow Wire Ignition Temperature, 30mil: 625 °C, Glow Wire Ignition Temperature, 40mil: 625 °C, Glow Wire Ignition Temperature, 60mil: 625 °C, Glow Wire Ignition Temperature, 80mil: 650 °C, Glow Wire Ignition Temperature, 120mil: 700 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.9 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 3.9 [-] | IEC 62631-2-1 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 4.4 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 4.4 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 0.04 [-] Show Material materials with Dissipation factor, 100Hz of 0.04 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Durchschlagfestigkeit | 23.0 °C | 34 kV/mm Show Material materials with Durchschlagfestigkeit of 34 kV/mm | IEC 60243-1 |
Kriechstromfestigkeit | 23.0 °C | 350 V Show Material materials with Kriechstromfestigkeit of 350 V | IEC 60112 |
Surface resistivity | 23.0 °C | 1.00E+14 Ω/sq Show Material materials with Surface resistivity of 1.00E+14 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+14 Ω·cm Show Material materials with Volume resistivity of 1.00E+14 Ω·cm | IEC 62631-3-1 |
Technological properties
| Property | ||
|---|---|---|
| Fillers | 15% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 285°C, Min. melt temperature: 270°C, Max. melt temperature: 290°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 95°C, Min. mold temperature: 75°C, Max. mold temperature: 95°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C | |