Eigenschaften
Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.53 g/cm³ Show Material materials with Dichte of 1.53 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 170 MPa Show Material materials with Biegefestigkeit of 170 MPa | ISO 178 |
Biegemodul | 23.0 °C | 5.94 GPa Show Material materials with Biegemodul of 5.94 GPa | ISO 178 |
Dehnung | 23.0 °C | 2.6 % Show Material materials with Dehnung of 2.6 % | ISO 527-1/-2 |
Druckfestigkeit | 23.0 °C | 170 MPa Show Material materials with Druckfestigkeit of 170 MPa | ISO 604 |
Elastizitätsmodul | 23.0 °C | 6.8 GPa Show Material materials with Elastizitätsmodul of 6.8 GPa | ISO 527-1/-2 |
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 |
Härte, Rockwell M | 23.0 °C | 88 [-] Show Material materials with Härte, Rockwell M of 88 [-] | ISO 2039-2 |
Poissonzahl | 23.0 °C | 0.35 [-] Show Material materials with Poissonzahl of 0.35 [-] | |
Scherfestigkeit | 23.0 °C | 50 MPa Show Material materials with Scherfestigkeit of 50 MPa | ASTM D 732 |
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 7 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 7 kJ/m² | ISO 179/1eA |
-6.0 °C | 7 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 7 kJ/m² | ISO 179/1eA | |
23.0 °C | 8 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 8 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -40.0 °C | 20 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 20 kJ/m² | ISO 179/1eU |
-6.0 °C | 35 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 35 kJ/m² | ISO 179/1eU | |
23.0 °C | 40 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 40 kJ/m² | ISO 179/1eU | |
Zugfestigkeit | 23.0 °C | 107 MPa Show Material materials with Zugfestigkeit of 107 MPa | ISO 527-1/-2 |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 240 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 240 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 200 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 200 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 1.2E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 1.2E-5 1/K | ISO 11359-1/-2 | 23 - 55°C | ||
Relative temperature index, electrical | 140 °C Show Material materials with Relative temperature index, electrical of 140 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical impact | 140 °C Show Material materials with Relative temperature index, mechanical impact of 140 °C | UL 746B | 120mil | |||
Relative temperature index, mechanical strength | 140 °C Show Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | 120mil | |||
Schmelzpunkt | 254 °C Show Material materials with Schmelzpunkt of 254 °C | ISO 11357-1/-3 | 18°F/min | |||
Vicat-Erweichungstemperatur | 210 °C Show Material materials with Vicat-Erweichungstemperatur of 210 °C | ISO 306 | 90°F/h, 11 lbf | |||
Wärmeleitfähigkeit | 23.0 °C | 0.25 W/(m·K) Show Material materials with Wärmeleitfähigkeit of 0.25 W/(m·K) | of solid | ||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 1E-4 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 1E-4 1/K | ISO 11359-1/-2 | 55 - 160°C | ||
Entflammbarkeit | Burning Behav. at thickness h: V-0 class, Thickness tested: 0.86 mm, UL recognition: yes -, Burning Behav. 5V at thickness h: 5VA class, Thickness tested: 1.5 mm, UL recognition: yes -, Oxygen index: 32 %, Glow Wire Flammability Index, 120mil: 960 °C, Glow Wire Ignition Temperature, 120mil: 875 °C, Glow Wire Temperature, No Flame, 40mil: 750 °C, Glow Wire Temperature, No Flame, 80mil: 650 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielektrizitätskonstante, 1 MHz | 23.0 °C | 3.5 [-] Show Material materials with Dielektrizitätskonstante, 1 MHz of 3.5 [-] | IEC 62631-2-1 |
Dielektrizitätskonstante, 100 Hz | 23.0 °C | 3.8 [-] Show Material materials with Dielektrizitätskonstante, 100 Hz of 3.8 [-] | IEC 62631-2-1 |
Dissipation factor, 100Hz | 23.0 °C | 9E-3 [-] Show Material materials with Dissipation factor, 100Hz of 9E-3 [-] | IEC 62631-2-1 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 62631-2-1 |
Durchschlagfestigkeit | 23.0 °C | 26 kV/mm Show Material materials with Durchschlagfestigkeit of 26 kV/mm | IEC 60243-1 | Short Time, 23°C, 2mm |
Kriechstromfestigkeit | 23.0 °C | 3 V Show Material materials with Kriechstromfestigkeit of 3 V | UL 746A |
Surface resistivity | 23.0 °C | 1.00E+13 Ω/sq Show Material materials with Surface resistivity of 1.00E+13 Ω/sq | IEC 62631-3-2 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Material materials with Volume resistivity of 1.00E+15 Ω·cm | min. | IEC 62631-3-1 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 15% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.02%, Melt Temperature Optimum: 280°C, Min. melt temperature: 270°C, Max. melt temperature: 290°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 110°C, Min. mold temperature: 100°C, Max. mold temperature: 120°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C | |