Allgemein
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dichte | 23.0 °C | 1.66 g/cm³ Show Material materials with Dichte of 1.66 g/cm³ | ISO 1183 |
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Biegefestigkeit | 23.0 °C | 280 MPa Show Material materials with Biegefestigkeit of 280 MPa | ISO 178 |
Biegemodul | 23.0 °C | 12 GPa Show Material materials with Biegemodul of 12 GPa | ISO 178 |
Dehnung | 23.0 °C | 2 % Show Material materials with Dehnung of 2 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 14 GPa Show Material materials with Elastizitätsmodul of 14 GPa | ISO 527-1/-2 |
Hardness, Ball Indentation | 23.0 °C | 225 MPa Show Material materials with Hardness, Ball Indentation of 225 MPa | ISO 2039-1 |
Hardness, Rockwell R | 23.0 °C | 120 [-] Show Material materials with Hardness, Rockwell R of 120 [-] | ISO 2039-2 |
Poissonzahl | 23.0 °C | 0.33 [-] Show Material materials with Poissonzahl of 0.33 [-] | |
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 9 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 9 kJ/m² | ISO 179/1eA |
-6.0 °C | 9 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 9 kJ/m² | ISO 179/1eA | |
23.0 °C | 9.5 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 9.5 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 55 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 55 kJ/m² | ISO 179/1eU |
Zugfestigkeit | 23.0 °C | 190 MPa Show Material materials with Zugfestigkeit of 190 MPa | ISO 527-1/-2 |
Thermisch
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 245 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 245 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 230 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 230 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 2E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 2E-5 1/K | ISO 11359-1/-2 | ||
Schmelzpunkt | 247 °C Show Material materials with Schmelzpunkt of 247 °C | ISO 11357-1/-3 | 18°F/min | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 7E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 7E-5 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | Glow Wire Flammability Index, 40mil: 750 °C, Glow Wire Flammability Index, 60mil: 750 °C, Glow Wire Flammability Index, 80mil: 750 °C, Glow Wire Flammability Index, 120mil: 850 °C, Glow Wire Ignition Temperature, 40mil: 750 °C, Glow Wire Ignition Temperature, 60mil: 750 °C, Glow Wire Ignition Temperature, 80mil: 750 °C, Glow Wire Ignition Temperature, 120mil: 850 °C, Glow Wire Temperature, No Flame, 40mil: 750 °C, Glow Wire Temperature, No Flame, 60mil: 750 °C, Glow Wire Temperature, No Flame, 80mil: 750 °C, Glow Wire Temperature, No Flame, 120mil: 850 °C, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||||
Elektrisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Durchschlagfestigkeit | 23.0 °C | 21.5 kV/mm Show Material materials with Durchschlagfestigkeit of 21.5 kV/mm | IEC 60243-1 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Schmelzmassenflussrate | 9 g/10min Show Material materials with Schmelzmassenflussrate of 9 g/10min | ISO 1133 | 280°C/2.16kg | |
Schrumpfung | 23.0 °C | 0.2 % Show Material materials with Schrumpfung of 0.2 % | ISO 294-4, 2577 |
Schrumpfung, diagonal | 23.0 °C | 0.9 % Show Material materials with Schrumpfung, diagonal of 0.9 % | ISO 294-4, 2577 |
Technological properties
| Property | ||
|---|---|---|
| Fillers | 36% Glass Fiber | |
| Processing methods | Drying Recommended: yes, Drying Temperature: 120°C, Drying Time, Dehumidified Dryer: 4-6h, Processing Moisture Content: ≤0.01%, Melt Temperature Optimum: 285°C, Min. melt temperature: 280°C, Max. melt temperature: 300°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 140°C, Min. mold temperature: 120°C, Max. mold temperature: 140°C, Hold pressure range: ≥80MPa, Hold pressure time: 4s/mm, Back pressure: As low as possible, Ejection temperature: 170°C | |