Allgemein
Property | Temperature | Value | Comment |
---|---|---|---|
Dichte | 23.0 °C | 1.46 g/cm³ Show Material materials with Dichte of 1.46 g/cm³ | ISO 1183 |
Wasserabsorption | 23.0 °C | 1.1 % Show Material materials with Wasserabsorption of 1.1 % | Sim. to ISO 62 | Immersion 24h |
Mechanisch
Property | Temperature | Value | Comment |
---|---|---|---|
Biegemodul | 23.0 °C | 5.3 GPa Show Material materials with Biegemodul of 5.3 GPa | ISO 178 |
Dehnung | 23.0 °C | 10 % Show Material materials with Dehnung of 10 % | ISO 527-1/-2 |
Elastizitätsmodul | 23.0 °C | 5.8 GPa Show Material materials with Elastizitätsmodul of 5.8 GPa | ISO 527-1/-2 |
Poissonzahl | 23.0 °C | 0.35 [-] Show Material materials with Poissonzahl of 0.35 [-] | |
Schlagfestigkeit, Charpy gekerbt | -40.0 °C | 3 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 3 kJ/m² | ISO 179/1eA |
23.0 °C | 6 kJ/m² Show Material materials with Schlagfestigkeit, Charpy gekerbt of 6 kJ/m² | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | 23.0 °C | 180 kJ/m² Show Material materials with Schlagzähigkeit, Charpy ungekerbt of 180 kJ/m² | ISO 179/1eU |
Schlagzähigkeit, Izod gekerbt | 23.0 °C | 95 kJ/m² Show Material materials with Schlagzähigkeit, Izod gekerbt of 95 kJ/m² | ISO 180/1U |
Schlagzähigkeit, Izod ungekerbt | -40.0 °C | 5 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 5 kJ/m² | ISO 180/1A |
23.0 °C | 6 kJ/m² Show Material materials with Schlagzähigkeit, Izod ungekerbt of 6 kJ/m² | ISO 180/1A | |
Zugfestigkeit | 23.0 °C | 86 MPa Show Material materials with Zugfestigkeit of 86 MPa | ISO 527-1/-2 |
Thermisch
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Heat deflection temperature, 0.45 MPa | 210 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 210 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 90 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 90 °C | ISO 75-1/-2 | |||
Koeffizient der thermischen Ausdehnung | 23.0 °C | 6.4E-5 1/K Show Material materials with Koeffizient der thermischen Ausdehnung of 6.4E-5 1/K | ISO 11359-1/-2 | ||
Relative temperature index, electrical | 65 °C Show Material materials with Relative temperature index, electrical of 65 °C | UL 746B | 60mil | |||
Relative temperature index, mechanical impact | 65 °C Show Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | 60mil | |||
Relative temperature index, mechanical strength | 65 °C Show Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | 60mil | |||
Schmelzpunkt | 256 °C Show Material materials with Schmelzpunkt of 256 °C | ISO 11357-1/-3 | 18°F/min | |||
thermischer Ausdehnungskoeffizient, transversal | 23.0 °C | 6.5E-5 1/K Show Material materials with thermischer Ausdehnungskoeffizient, transversal of 6.5E-5 1/K | ISO 11359-1/-2 | ||
Entflammbarkeit | Burning Behav. at 60mil nom. thickn.: HB class, Thickness tested: 1.5 mm, UL recognition: yes -, Burning Behav. at thickness h: HB class, Thickness tested: 0.81 mm, UL recognition: yes -, FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Fillers | 40% Mineral Powder | |
Processing methods | Drying Recommended: yes, Drying Temperature: 80°C, Drying Time, Dehumidified Dryer: 2-4h, Processing Moisture Content: ≤0.2%, Melt Temperature Optimum: 295°C, Min. melt temperature: 285°C, Max. melt temperature: 305°C, Max. screw tangential speed: 0.2m/s, Mold Temperature Optimum: 100°C, Min. mold temperature: 70°C, Max. mold temperature: 120°C, Hold pressure range: 50-100MPa, Hold pressure time: 3s/mm, Ejection temperature: 210°C |